Abstract:High-quality zeolite silicalite-1 membranes with a large area (78.5cm2) were successfully prepared on porous, tubular stainless steel (PTSS) supports with optimized synthesis solution composition by a two-stage varying-temperature in situ synthesis. Compared with the synthesis at constant temperature (one-stage), the two-stage varying-temperature in situ synthesis (TSVTS) generated a thin and dense membrane, since a large number of new nuclei could form at low temperature, while the crystallization temperature was rapidly changed to a high temperature after completion of the nucleation period, a thin and continuous membrane would quickly formed on the support by the nuclei regrowth. The membranes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single-gas permeation. These results indicate that the membranes prepared by the TSVTS method exhibit high gas permeation performance and good reproducibility. H2 permeance and H2/n-C4H10 selectivity of the membranes by TSVTS method reached to 12.25×10−7mol/(m2sPa) and 46.1, respectively. And the yield of high-quality membranes with perm-selectivity of H2/n-C4H10 larger than 25 (which is almost five times as large as the Knudsen factor) as a quality criterion reached to 70% of all preparations. By comparison of their permeability and reproducibility with those reported in the literature, it was revealed that the prepared membranes by TSVTS method were of good quality. Moreover, their thermal stability were tested in a gas mixture of ethylbenzene and hydrogen at high temperature, for an example, the membrane having the separation selectivity of hydrogen and ethylbenzene mixture as high as 190 is stable after 80h of run at 400°C, suggesting the membrane is thermally durable for long time operation.

Preparation and characterization of silicalite-1 membrane by counter-diffusion secondary growth

A Novel Method to Synthesize High Performance Silicalite-1 Membrane

Synthesis and property of silicalite-1 membranes by restricting growth method with dilute solution

Preparation of silicalite-1 zeolite membrane on porous α-Al2O3 tube by modified secondary growth method and its characterization

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Synthesis of Silicalite-1 Zeolite Membrane by Nanocrystal Seed Coating Method

SYNTHESIS OF SILICALITE-1 MEMBRANE BY A NOVEL EMBELLISHING METHOD AND ITS GAS PERMEANCE

Preparation and characterization of silicalite-1 membrane on a silicalite-1/TiO2 composite layer

Synthesis of Silicalite-1 Zeolite Membrane with Vacuum Seeding Method and Its Characterization of Performance

Preparation of mesoporous MCM-48 membrane by counter-diffusion growth process

Synthesis of silicalite-1 membrane with two silicon source by secondary growth method and its pervaporation performance

Preparation of Microfibrous Supported Silicalite-1 Zeolite Membrane by Secondary Growth Method

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Synthesis and Characterization of High - Selectivity, High - Flux Silicalite- 1 Zeolite Membrane

Preparation and Gas Permeance Separation Property of Silicalite- 1 Zeolite Membrane with Low- Template Method

Synthesis and structural analysis of Silicalite-1 membranes by coating technique with nanosized seed

Liquid Phase Oxidation and Low-Temperature Calcination Method for Organic Template Removal from Silicalite-1 Membrane and Its Performance

Transfer Printing Platelike MFI Crystals As Seeds for the Preparation of Silicalite-1 Membranes

Preparation of Silicalite-1 Membranes on Stainless Steel Supports by a Two-Stage Varying-Temperature in Situ Synthesis

Preparation of Silicalite-2 Zeolite Membrane on Macroporous Support by Seeded Steam-assisted Crystallization Method

Synthesis and characterization of a mesoporous silica (MCM-48) membrane on a large-pore α-Al2O3 ceramic tube