Preparation of mesoporous MCM-48 membrane by counter-diffusion growth process

LIU Chunyan,LIU Jiale,WANG Jinqu,LU Jinming,YANG Jianhua,ZHANG Yan
DOI: https://doi.org/10.3969/j.issn.1007-8924.2012.06.010
2012-01-01
Abstract:Mesoporous silica MCM-48 membranes have been synthesized on a coarse-pore α-Al2O3 ceramic tube by counter-diffusion growth process(CDGP).First,MCM-48 seeds were prepared by hydrothermal synthesis using CTAB and P123 as co-templates,and TEOS as silica source.Then the seed aqueous solution was prepared and coated on outer surface of the preheated supports by dip-coating technique to form a continuous seed layer.And then MCM-48 membrane was prepared using the CDGP method.Different from the conventional synthesis methods by which the silica source and the template agent were mixed together to form the synthesis solution,the CDGP method introduced silica source and template agent from the opposite direction of a support wall,resulting in good membrane structures and properties.The seeds and MCM-48 membrane were characterized by small-angle X-ray diffraction,SEM measurement and gas permeation tests.XRD patterns showed the seeds had a typical MCM-48 XRD patterns.SEM analysis revealed that the MCM-48 membranes were dense,continuous and without obvious defects,indicating good permeation property.At room temperature,the separation selectivity of H2/N2 was up to 3.0 under 0.1 MPa pressure drop.
What problem does this paper attempt to address?