Abstract:High-quality zeolite silicalite-1 membranes with a large area (78.5cm2) were successfully prepared on porous, tubular stainless steel (PTSS) supports with optimized synthesis solution composition by a two-stage varying-temperature in situ synthesis. Compared with the synthesis at constant temperature (one-stage), the two-stage varying-temperature in situ synthesis (TSVTS) generated a thin and dense membrane, since a large number of new nuclei could form at low temperature, while the crystallization temperature was rapidly changed to a high temperature after completion of the nucleation period, a thin and continuous membrane would quickly formed on the support by the nuclei regrowth. The membranes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single-gas permeation. These results indicate that the membranes prepared by the TSVTS method exhibit high gas permeation performance and good reproducibility. H2 permeance and H2/n-C4H10 selectivity of the membranes by TSVTS method reached to 12.25×10−7mol/(m2sPa) and 46.1, respectively. And the yield of high-quality membranes with perm-selectivity of H2/n-C4H10 larger than 25 (which is almost five times as large as the Knudsen factor) as a quality criterion reached to 70% of all preparations. By comparison of their permeability and reproducibility with those reported in the literature, it was revealed that the prepared membranes by TSVTS method were of good quality. Moreover, their thermal stability were tested in a gas mixture of ethylbenzene and hydrogen at high temperature, for an example, the membrane having the separation selectivity of hydrogen and ethylbenzene mixture as high as 190 is stable after 80h of run at 400°C, suggesting the membrane is thermally durable for long time operation.

Preparation and Gas Permeance Separation Property of Silicalite- 1 Zeolite Membrane with Low- Template Method

ZSM-5 zeolite membranes prepared from a clear template-free solution

Synthesis and Characterization of High - Selectivity, High - Flux Silicalite- 1 Zeolite Membrane

Synthesis of Silicalite-1 Zeolite Membrane by Nanocrystal Seed Coating Method

SYNTHESIS OF SILICALITE-1 MEMBRANE BY A NOVEL EMBELLISHING METHOD AND ITS GAS PERMEANCE

Preparation and characterization of silicalite-1 membrane on a silicalite-1/TiO2 composite layer

Preparation of silicalite-1 zeolite membrane on porous α-Al2O3 tube by modified secondary growth method and its characterization

Liquid Phase Oxidation and Low-Temperature Calcination Method for Organic Template Removal from Silicalite-1 Membrane and Its Performance

Synthesis and property of silicalite-1 membranes by restricting growth method with dilute solution

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Synthesis of Silicalite-1 Zeolite Membrane with Vacuum Seeding Method and Its Characterization of Performance

Preparation and characterization of silicalite-1 membrane by counter-diffusion secondary growth

A Novel Method to Synthesize High Performance Silicalite-1 Membrane

Synthesis and Low-Temperature Detemplation of High-Silica Mfi Zeolite Membranes

Preparation and permeability performances of MFI zeolite membranes by in-situ crystallization method

Study on Preparation and Gas Permeation Property of MFI Type Zeolite Membrane

Preparation and Pervaporation Performance of Silicalite-1 Zeolite Membrane with a Two-stage Temperature-varied Hydrothermal Technique

Preparation of Silicalite-1 Membranes on Stainless Steel Supports by a Two-Stage Varying-Temperature in Situ Synthesis

Fast synthesis of thin Silicalite-1 zeolite membranes at low temperature

Permeation and Separating Properties of Small Molecule Inorganic Gases on NaA Zeolite Membrane

Synthesis of silicalite-1 zeolite membranes for vapor-permeation separation of dichlorobenzene Isomers