Microwave dielectric properties of the (1−x)Mg2TiO4–xCaTiO3–y wt.% ZnNb2O6 ceramics system

Hui Zhu,Wen-Zhong Lu,Wen Lei

DOI: https://doi.org/10.1016/j.ceramint.2011.01.015

IF: 5.532

2011-01-01

Ceramics International

Abstract:Composite ceramics based on (1−x)Mg2TiO4–xCaTiO3–y wt.% ZnNb2O6 (x=0.12–0.16, y=0–8) were prepared by a conventional mixed-oxide route. Zn2+ partially replaced Mg2+ in Mg2TiO4 and formed the spinel-structured (Mg1−δZnδ)2TiO4 phase. Nb2+, is known to be solid soluble in CaTiO3, was found to change its shape from cubic to pliable. A bi-phase system (Mg1−δZnδ)2TiO4 and CaTiO3 exhibited in all samples, where a small amount of second phase Mg1−δZnδTiO3 was also detected. The microwave dielectric properties of specimens were strongly related to ZnNb2O6 and CaTiO3 content. As y increased, ɛr and τf decreased, however, Q×f decreased to a minimum value and started to increase thereafter. It was also found that ɛr and τf increased and Q×f decreased with increasing x. The optimized microwave dielectric properties with ɛr=18.37, Q×f=31,027GHz (at 6GHz), and τf=0.51ppm/°C were achieved for (1−x)Mg2TiO4–xCaTiO3–y wt.% ZnNb2O6 (x=0.12, y=4) sintered at 1360°C for 6h.