Abstract:Phase selection and microstructure evolution of the undercooled eutectic Ti-Si alloy were systematically investigated by the electromagnetic levitation method, and the maximum undercooling achieved was 318 K (0.2 T E ). The migration of the liquid-solid interface was in-situ detected by a high-speed camera system. When the undercooling is smaller than 140 K, the liquid-solid interface is smooth. Once the undercooling arrives at 230 K, the liquid-solid interface is irregular, which reflects the growth transition from the solute control to the combined controls of solute and thermal. The eutectic growth velocity increases as an exponential function of undercooling. The electromagnetic stirring effect makes it difficult to increase undercooling, but plays an important role in accelerating the eutectic reaction velocity at low and moderate undercoolings. Primary dendritic β-Ti phase appears in the solidified alloy from 63 to 176 K undercoolings, and the microstructure is completely composed of eutectic once the undercoolings increase up to 230 K. When the undercoolings exceed 273 K, the microstructure consists of uniformly distributed irregular eutectic. For the drop tube experiments, the microstructures composed of a large amount of dendritic α-Ti phase and eutectic phase are found in a wide range of diameters from 69 to 725 μm. As the decrease of diameter, the solubility of Si in the dendritic α-Ti phase dramatically increases from 6.80% to 10.73%, and the ratio of the area occupied by the dendritic α-Ti on a cross-section of solidified alloy obviously increases from 23.52% to 41.02%, which result from the combined effects of high undercooling and large cooling rate.

Rapid Eutectic Growth During Free Fall

Solidification of Undercooled Ag–Cu Eutectic Alloy with the Sb Addition

Rapid Dendritic Growth in an Undercooled Ni—Cu Alloy under the Microgravity Condition

The Growth Velocity-Undercooling Relationship of Highly Undercooled Ni and Ni-Cu Melts

Growth Velocity-Undercooling Relationship and Structure Refinement Mechanism of Undercooled Ni-Cu Alloys

Cellular Growth of Lamellar Eutectics in Undercooled Ag–Cu Alloy

Solidification behavior and microstructure of Ag–Cu eutectic alloy at different sub-rapid cooling rates

Evolution Mechanism of Rapid Solidification Microstructure of an Undercooled Copper-Based Single Phase Alloy

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

Structural Evidence for the Transition from Coupled to Decoupled Growth in the Solidification of Undercooled Ni-Sn Eutectic Melt

Solidification Microstructure in a Supercooled Binary Alloy

Rapid Solidification of Cu60Co30Cr10 Alloy under Different Conditions

Phase selection and microstructure evolution within eutectic Ti-Si alloy solidified at containerless state

Rapid Solidification of Non-Stoichiometric Intermetallic Compounds: Modeling and Experimental Verification

Primary Phase Growth and Microstructure Evolution of Rapidly Solidifying Ternary Ti-12Al-8V Alloy

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Revealing the Nucleation and Growth Modes Upon Rapid Solidification of Undercooled Co-24 At.% Sn Eutectic Alloy by the Crystallographic Orientation Relations

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Rapid Dendritic Growth and Solute Trapping Within Undercooled Ternary Ni-5%Cu-5%Mo Alloy

Formation Mechanism of Anomalous Eutectics in Highly Undercooled Ag-39.9 At%Cu Alloys

Effect of rapid quenching on Sb grain-boundary segregation in Cu