Abstract:1. Experimental Section Preparation of the glasses: The two kinds of glass samples used in our experiment were both prepared by the melting-quenching technique. Initially, the glasses without AgNO3 (NAG) were prepared using the following composition: 66SiO2-8B2O3-18K2O-6ZnO-1ZnS-1PbO (in mol %). The mixture of analytical grade raw materials SiO2, B2O3, K2CO3, ZnO, ZnS and PbO were melted at 1450 oC in an alumina crucible for 90min under ambient conditions, quenched in a preheated brass mold and annealed at 400 oC for 1 h. As to the other kind of glass, when melting extra 20 ppm (in mol %) AgNO3 (AG) was added in compared to the first kind of glass and the fabrication process is the same with the glass without AgNO3. Heat-treatment of the as-prepared glasses and its characterizations: The as-prepared two kinds of glasses both with slight yellow color were cut and further annealed at 540 oC, 560 oC and 580 oC for different durations. After heat treatment, the samples were cooled to room temperature inside the furnace and then polished into a plate of 1 mm thick to make further characterizations. The photoluminescence spectra were measured on a Triax 320 spectrometer (Jobin-Yvon Co., France) with a resolution of 1 nm, which were excited by a 976 nm laser diode (LD) and detected with a PbSe photodetector. Optical transmittance spectra of glass composites were recorded on a UV/VIS/NIR spectrophotometer (Lambda-900, Perkin-Elmer, USA). The confocal Raman spectra from the heat treated samples with a 785 nm laser as the excitation source were measured by a

Preparation and optical properties of silicate glasses containing Pd nanoparticles

Effect of Pbo on Precipitation of Laser-Induced Gold Nanoparticles Inside Silicate Glasses

Space-Selective Co-Precipitation of Silver and Gold Nanoparticles in Femtosecond Laser Pulses Irradiated Ag+, Au3+ Co-Doped Silicate Glass

Precipitation of metallic nanoparticles inside silicate glasses by femtosecond laser pulses

Direct Space Selective Precipitation of Silver Nanoparticles Inside Silicate Glasses Through Local Heating of Erbium

Space-Selective Precipitation Of Silver Nanoparticles In Ag2o Doped Silicate Glass By Irradiation Of Femtosecond Laser

Space-Selective Precipitation of Metal Nanoparticles Inside Glasses

Laser-controlled precipitation of gold nanoparticles in silicate glasses

A Study on the Photo-Induced Crystallization Properties in Au+-Doped Silicate Glasses

Effect of PbO on Precipitation of Laser-induced Au Nanoparticles Inside Glasses

Controllable Precipitation and Dissolution of Silver Nanoparticles in Ultrafast Laser Pulses Irradiated Ag+-doped Phosphate Glass.

Effect of Al2O3 on the precipitation of Ag nanoparticles in silicate glasses

Pd Nanoparticles Formation by Femtosecond Laser Irradiation and the Nonlinear Optical Properties at 532 Nm Using Nanosecond Laser Pulses

Space-Selective Precipitation of Gold Nanoparticles in Glass Induced by Femtosecond Laser and Spectra Properties

Formation, near-infrared luminescence and multi-wavelength optical amplification of PbS quantum dot-embedded silicate glasses

Dependence of Femtosecond Laser Irradiation and Heat Treatment on Gold Nanoparticle Precipitation in Silicate Glass

Tunable Infrared Luminescence and Optical Amplification in PbS Doped Glasses

Formation and selective micron-region control of PbS quantum dots inside glasses using femtosecond laser pulses

Formation and Selective Micron-Regional Control of PbS Quantum Dots in Glasses Using Femtosecond Laser Pulsation

Optical Nonlinearities of Space Selectively Precipitated Au Nanoparticles Inside Glasses

Palladium Speciation in UV‐transparent Glasses