Abstract:We report the precipitation and control of metal nanoparticles inside transparent glasses. An Ag+-doped silicate glass sample was first irradiated by using an 800 nm femtosecond laser at room temperature and then annealed at 550 °C. The area near the focal point of the laser beam became gray after laser irradiation and yellow after further annealing at 550 °C for 10 min. Absorption and electron spin resonance spectra of the glass sample showed that a portion of silver ions near the focused part of the laser beam inside the glass were reduced to silver atoms after the laser irradiation. These silver atoms aggregated to form nanoparticles after further annealing at temperatures above 500 °C. A mechanism is suggested that consists of multiphoton reduction, which is induced by the fundamental light of the laser beam and supercontinuum white light, and diffusion of silver atoms driven by heat energy to form nanoparticles. The observed phenomenon may have promising applications for the fabrication of three-dimensional multicolored images inside a transparent material and for integrative micro-optical switches.

Space-Selective Precipitation Of Silver Nanoparticles In Ag2o Doped Silicate Glass By Irradiation Of Femtosecond Laser

Laser-controlled precipitation of gold nanoparticles in silicate glasses

Space-Selective Co-Precipitation of Silver and Gold Nanoparticles in Femtosecond Laser Pulses Irradiated Ag+, Au3+ Co-Doped Silicate Glass

Space-Selective Precipitation of Metal Nanoparticles Inside Glasses

Controllable Precipitation and Dissolution of Silver Nanoparticles in Ultrafast Laser Pulses Irradiated Ag+-doped Phosphate Glass.

Direct Precipitation of Silver Nanoparticles Induced by a High Repetition Femtosecond Laser

Space-Selective Precipitation of Gold Nanoparticles in Glass Induced by Femtosecond Laser and Spectra Properties

Direct Space Selective Precipitation of Silver Nanoparticles Inside Silicate Glasses Through Local Heating of Erbium

SPACE-SELECTIVE PRECIPITATION OF GOLD NANOPARTICLES IN TRANSPARENT GLASSES

Influence Of Femtosecond Laser Irradiation And Heat Treatment On Precipitation Of Silver Nanoparticles In Glass

Precipitation of metallic nanoparticles inside silicate glasses by femtosecond laser pulses

The Effect Of Femtosecond Laser Irradiation Conditions On Precipitation Of Silver Nanoparticles In Silicate Glasses

Dependence of Femtosecond Laser Irradiation and Heat Treatment on Gold Nanoparticle Precipitation in Silicate Glass

Metal Nanoparticle Precipitation In Periodic Arrays In Au2o-Doped Glass By Two Interfered Femtosecond Laser Pulses

Effect of Al2O3 on the precipitation of Ag nanoparticles in silicate glasses

Controllable Space Selective Precipitation of Copper Nanoparticles in Borosilicate Glasses Using Ultrafast Laser Irradiation

Space-selective Crystallization of Glass Induced by Femtosecond Laser Irradiation

Preparation and optical properties of silicate glasses containing Pd nanoparticles

Femtosecond laser induced space-selective precipitation of Cr3+-doped ZnAl2O4 crystal in glass

Space-Selective Precipitation Of Zno Crystals In Glass By Using High Repetition Rate Femtosecond Laser Irradiation

Space-Selective Precipitation of Au Nanoparticles Inside Silica Gel