Abstract:To understand the stress state dependent creep damage, following creep tests in 9–12% Cr steel notched components with different root radii, a study of associated time dependent microstructural evolution is presented in this work. Particular attention is paid to the dependence of creep damage evolution on the stress state. The average creep strain of notched component exhibits a typical three-stage characteristic (transient, steady and tertiary stages). During the transient stage, remarkable re-distribution in stress state (equivalent stress and stress triaxiality) is found. The rapid relaxation of equivalent stress near the notch root, associated with the initial coarsening of substructure would delay the nucleation or growth of cavity. By contrast, the time-dependent increase of equivalent stress combined with the relatively high stress triaxiality seems to be responsible for the higher cavity density at the center of notched component. The precipitate coarsening is heterogeneous and promoted by the high level of equivalent stress or stress triaxiality. During the steady stage, the creep damage behavior is related to the magnitude of stress state. Higher cavity density and greater reduction in hardness are mainly found in the region where both the equivalent stress and stress triaxiality are high. As a whole, both the redistribution process of stress states and their levels exhibit significant influence on microstructural evolution and creep damage behavior of notched components at elevated temperatures.

Development of Tensile and Creep Properties for FGH95 Little Notched Specimens at High Temperature

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Influence of Notch on Creep Properties of GH3536 Nickel-Based Superalloy

Creep Properties of V-notched Round Rod Specimen under Triaxial Stress State

Fracture Behaviour of Compact Tension Specimens of Nickel-based Single Crystal Under Tension Creep and Cyclic Loading

Stress State Dependent Creep Damage Behavior of 9–12% Cr Steel Notched Components

A Unified Creep Life Prediction Method and Fracture Mechanism of High-Temperature Alloys under Multiaxial Stress

A unified creep life prediction method and fracture mechanism for different notch acuity ratios round bars of high-temperature alloys under multiaxial stress state

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

On the Study of the Creep Damage Development in Circumferential Notch Specimens

Low cycle fatigue and creep-fatigue behavior of a high temperature alloy on smooth and notched specimens

A unified creep life prediction method and fracture mechanism of high-temperature alloys under multiaxial stress state

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

On the Study of the Effects of Notch Shape on Creep Damage Development under Constant Loading

Creep Damage Mechanism and Γ′-Phase Morphology of a V-notched Round Bar in Ni-based Single Crystal Superalloys

Determination of Creep Crack Growth Threshold by Experiments under Elevated Temperature with Pre-Stressed Specimens

Finite Element Stress and Strain Analysis of a Double Shear Creep Specimen

Effects of Creep Ductility and Notch Constraint on Creep Fracture Behavior in Notched Bar Specimens

Notch Effect on Structural Strength of Components at Elevated Temperature under Creep, Fatigue, and Creep-Fatigue Loading Conditions: Phenomenon and Mechanism

Creep Damage in 9-12% Cr Steel Notched Components: Microstructural Evolution and Stress State Dependence

Numerical simulation of creep notched bar of P91 steel