Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Electrospinning Preparation, Structure, and Photoluminescence Properties of YBO<sub>3</sub>:Eu<sup>3+</sup>Nanotubes and Nanowires

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

White-light Emission and Weak Antiferromagnetism from Cubic Rare-Earth Oxide Eu2O3 Electrospun Nanostructures

Electrodeposition and luminescent properties of YBO 3 :Eu 3+ and Y 3 BO 6 :Eu 3+ films

Size Dependence of Luminescent Properties for Hexagonal YBO3:Eu Nanocrystals in the Vacuum Ultraviolet Region

Fabrication and optical properties of Y2O3: Eu3+ nanofibers prepared by electrospinning.

Hydrothermal Synthesis and Characterization of Flowerlike YBO_3∶Eu~(3+)

Fluorescence Intensity and Color Purity Improvement in Nanosized Ybo3 : Eu

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Improved Luminescent Properties of Novel Nanostructured Eu3+ Doped Yttrium Borate Synthesized with Carbon Nanotube Templates

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Hydrothermal synthesis and tunable luminescence of YPO4:Eu2+/Eu3+, Tb3+ nanocrystals

Facile synthesis of Y4O(OH)9NO3:Eu 3+/Y2O3:Eu3+ nanotubes and nanobundles from nanolamellar precursors

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Facile synthesis of Y<sub>4</sub>O(OH)<sub>9</sub>NO<sub>3</sub>:Eu3+/Y<sub>2</sub>O<sub>3</sub>:Eu3+nanotubes and nanobundles from nanolamellar precursors

Controllable Synthesis and Size-Dependent Luminescent Properties of YVO<sub>4</sub>:Eu<sup>3+</sup>Nanospheres and Microspheres

Solvothermal route to synthesize well-dispersed YBO3:Eu nanocrystals.

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS