Superplastic components of naphthalenic pumping admixture influencing on slag cement

WANG Liang,YANG Yan-ying,FAN Ya-jun,ZHOU Yong

DOI: https://doi.org/10.3969/j.issn.1002-3550.2009.10.028

2009-01-01

Abstract:In Portland cement which has Gongyuan 32.5 levels,when the content of Sodium tripolyphosphate increases,the slump retaining ability will be higher.This mixture has some retarding effects and it reduces the early strength of concrete,however the later strength will increase to a reasonable level.The optimum concentration of Sodium hexametaphosphate is between 0.05% and 0.10% to provide the best slump retaining ability,better retarding effects and higher later strength.The optimum level of Sugar Sodium is 0.15%,but the slump retaining ability remains at a reasonably high level when it is between 0.05% and 0.15%.As the content of Sugar Sodium increases,the strength of 3 d and 28 d concrete will also decrease.When the level is at 0.05%,the strength of 3 d and 28 d concrete can reach 19.0 MPa and 38.6 MPa,which are 21.0% and 9.3% higher than the blank test results respectively.The optimum content of Sodium Gluconate is 0.05%,the compression strength of concrete can arrive 44.8 MPa which is 26.2% higher than the blank test result.Silicone can not provide better slump retaining ability in Gongyuan 32.5 levels Portland cement.When the content of T11-904 is 0.10%,it can provide the optimum slump retaining ability and significant retarding effects,but the strength development is not ideal within 28 days.The content of ATMP will reach its saturation point when the content is 0.05%,the strength of 28 d concrete will increase as the amount of ATMP increase.The content of HEDP should be keeping within 0.05%,it will have some certain level of retarding effects.