Abstract:In Portland cement which has Gongyuan 32.5 levels,when the content of Sodium tripolyphosphate increases,the slump retaining ability will be higher.This mixture has some retarding effects and it reduces the early strength of concrete,however the later strength will increase to a reasonable level.The optimum concentration of Sodium hexametaphosphate is between 0.05% and 0.10% to provide the best slump retaining ability,better retarding effects and higher later strength.The optimum level of Sugar Sodium is 0.15%,but the slump retaining ability remains at a reasonably high level when it is between 0.05% and 0.15%.As the content of Sugar Sodium increases,the strength of 3 d and 28 d concrete will also decrease.When the level is at 0.05%,the strength of 3 d and 28 d concrete can reach 19.0 MPa and 38.6 MPa,which are 21.0% and 9.3% higher than the blank test results respectively.The optimum content of Sodium Gluconate is 0.05%,the compression strength of concrete can arrive 44.8 MPa which is 26.2% higher than the blank test result.Silicone can not provide better slump retaining ability in Gongyuan 32.5 levels Portland cement.When the content of T11-904 is 0.10%,it can provide the optimum slump retaining ability and significant retarding effects,but the strength development is not ideal within 28 days.The content of ATMP will reach its saturation point when the content is 0.05%,the strength of 28 d concrete will increase as the amount of ATMP increase.The content of HEDP should be keeping within 0.05%,it will have some certain level of retarding effects.

The influence of fast-setting/early-strength agent on high phosphorous slag content cement

Application investigation of high-phosphorus steel slag in cementitious material and ordinary concrete

EARLY HYDRATION CHARACTERISTICS AND PASTE STRUCTURE OF COMPLEX BINDING MATERIAL CONTAINING HIGH-VOLUME STEEL SLAG

Experimental study on strength and abrasion-resistance enhancement admixture

Influences of Phosphorous Slag As Cement Replacement on the Performances of Recycled Aggregate Concrete

Setting Time Optimization of Excessive-Sulfate Phosphogypsum Slag Cement for Self-Compacting Concrete Based on a Paste Rheological Threshold Theory

The influence of steel slag with high Al 2 O 3 content on the initial hydration of cement

Hydration and Properties of Magnesium Potassium Phosphate Cement Modified by Granulated Blast-Furnace Slag: Influence of Fineness

Investigation on mechanical properties of excess-sulfate phosphogypsum slag cement: From experiments to molecular dynamics simulation

Study on properties of inorganic grouting material modified by ultrafine slag powder

Hydration kinetics and microstructure development of Ultra-High Performance Concrete (UHPC) by high volume of phosphorus slag powder

Superplastic components of naphthalenic pumping admixture influencing on slag cement

Effect of ultrafine slag on hydration heat and rheology properties of Portland cement paste

Effect of calcium sulfoaluminate cement on the hydration process and water resistance of phosphogypsum slag cement

The influence of superplasticizer and superfine mineral powder on the flexibility, strength and durability of HPC

Physico-chemical Characteristics of Wet-milled Ultrafine-granulated Phosphorus Slag as a Supplementary Cementitious Material

Understanding the multiple actions of phosphoric acid-modified steel slag powder on early-age hydration of cement

Study on the properties of alkali-activated phosphorus slag mortar mixed with granulated blast furnace slag/fly ash

Greener phosphogypsum-based all-solid-waste cementitious binder with steel slag activation: Hydration, mechanical properties and durability

An Eco-Friendly Phosphogypsum-Based Cementitious Material: Performance Optimization and Enhancing Mechanisms

Insight into the performance of composite binder with high-volume steel slag, blast furnace slag and desulfurization gypsum