Abstract:The paper comprehensively describes the evolution of metastable microstructures in a cast low-Ta-containing γ-TiAl alloy during cooling-tempering-lamellarization heat treatments. The behavior and mechanism of microstructure refinement are discussed. The rapid cooling generates metastable microstructures, including Widmanstätten, feathery, and massive structures, with many γ variants in small sizes and different orientations. It significantly refines the coarsened colonies and randomizes the texture. The tempering can effectively stabilize the metastable microstructures. During tempering, the γ→α phase transformation is more active at higher temperatures while coarsening and recrystallization dominate at lower temperatures. After tempering, a refined microstructure with spherical grains and convoluted structures forms. Subsequent lamellarization treatment optimizes the microstructure and obtains a fine-grained nearly-lamellar microstructure with small colonies (∼70 μm) and dispersed fine γ grains (∼10 vol%), which yielded a 1.0 % elongation with a 487 MPa yield strength (0.2%) and a 589 MPa ultimate tensile strength at room temperature. Finally, the unique promotion effects and mechanism of a small amount of Ta addition on the nucleation, growth, evolution, and stabilization of metastable microstructures are concluded and discussed, which is crucial for the refinement of cast γ-TiAl alloy by heat treatment alone.

Grain refinement of a Ti–47Al–8Nb–2Cr alloy through heat treatments

On the grain size refinement of TiAl alloys by cyclic heat treatment

Grain refinement of a TiAl alloy by heat treatment through near gamma transformation

Effect of cooling rate on the grain refinement of TiAl-based alloys by rapid heat treatment

Effect of heating rate on the grain refinement of a TiAl alloy by cyclic heat treatment

Refining grain size of a TiAl alloy by cyclic heat treatment through discontinuous coarsening

Grain refinement of 1 at.% Ta-containing cast TiAl-based alloy by cyclic air-cooling heat treatment

Refining grain of as-cast Ti46A18Nb alloy by heat treatment

Control of the homogeneity of the lamellar structure of a TiAl alloy refined by heat treatment

Grain Refinement Mechanism at High Undercooling of Ni80Cu20 Alloy

Microstructure refinement of a TiAl alloy by beat treatment

Cycling Heat Treatment Refinement the Grain Size of a TiAl - Base Alloy

Metastable microstructure evolution and grain refinement in a Low-Ta containing γ-TiAl alloy through heat treatment

Refinement mechanism of centimeter-grade coarse grains in as-cast Ti 2 AlNb-based alloy during multi-directional forging

Grain Refinement of Al-5Ti-0.62C-0.2Nd Grain Refiner for Commercial Pure Aluminum and Its Effect on Mechanical Properties

Refinement Mechanism of Centimeter-Grade Coarse Grains in As-Cast Ti2AlNb-based Alloy During Multi-Directional Forging

Grain Refinement Mechanisms of TiC0.5N0.5 Nanoparticles in Aluminum

The Effect of Heat Treatment on the Microstructure of Ti-45Al-5Nb-0.3Y Alloy

Grain Refinement by Trace Tib2 Addition in Conventional Cast Tial-Based Alloy

A Novel Method and Mechanism for Simultaneously Refining Microstructure and Controlling Grain Orientation in Ti48Al2Cr2Nb2.5C Alloy

Microstructure refinement of Ti-40Al-8Nb alloys via the decomposition of the metastable B2 phase at 1000 °C