Abstract:The particle/matrix interface of metal matrix composites (MMCs) can give rise to extra strength and then affect the local deformation behavior. This strengthening effect originates from the plastic strain gradients due to the incompatibility of plastic deformation between the particle and matrix. However, only limited researches utilized the strain gradient plasticity to study the damage evolution and fracture behavior, in which only one or two of the damage mechanisms (i.e., matrix damage, interface debonding, and particle fracture) was considered. In this work, all of these damage mechanisms were coupled into the finite element model under conventional theory of mechanism-based strain-gradient (CMSG) plasticity. Besides, a new numerical algorithm of geometrically necessary dislocations (GNDs) was proposed for a multi-scale model, and then this model was used to analyze the damage evolution and failure behavior of SiCp/AZ91 composite. The results show that the strengthening effects of plastic strain gradients can describe interface debonding, break the monotonicity of the effective plastic strain with the effective stress at the local area close to the particle/matrix interface, and give a more reasonable distribution of stress and plastic strain compared to the classical J2 flow theory. If the probability distribution of the interfacial strength is considered, the CMSG model has the potential capacity to capture the crack initiation in the matrix. When using the continuum damage mechanics approach to describe the fracture process based on the multi-scale model, the weakening exponent value should be considered.

A numerical strength analysis of metal matrix composites considering the interface and matrix damage evolution

Micro Failure Analysis of Fiber Metal Laminates

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Modeling of Progressive Failure in Ductile Matrix Composites Including Local Matrix Yielding

Probabilistic Analysis for Tensile Failure of Metal Matrix Composites.

A coupled ductile damage model for metal matrix composites: Development and application

Micro numerical simulation of creep damage and failure of short fiber reinforced metal matrix composites (MMCs)

Transverse Strength Prediction of Composite Materials Via Micromechanics Model

Micromechanical modeling of damage evolution and fracture behavior in particle reinforced metal matrix composites based on the conventional theory of mechanism-based strain gradient plasticity

INTERFACE DAMAGE ANALYSIS OF FIBER-REINFORCED COMPOSITES WITH DUCTILE MATRIX

A Study of Interface Damage on Mechanical Properties of Particle-Reinforced Composites

A new constitutive model of micro-particle reinforced metal matrix composites with damage effects

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

Micromechanical Analysis of Transverse Damage of Fibre-Reinforced Composites

Damage of Short-Fiber-Reinforced Metal Matrix Composites Considering Cooling and Thermal Cycling

Damage micromechanical analysis of metal matrix composites

Meso-fracture of Metal Matrix Composites Reinforced by Particles of Large Volume Fraction

Irreversible Deformation of Metal Matrix Composites: A Study Via the Mechanism-Based Cohesive Zone Model

A Microscopic Dynamic Monte Carlo Simulation for Unidirectional Fiber Reinforced Metal Matrix Composites

Micromechanical Modeling of the Effect of Progressive Damage on the Tensile Behavior in Fiber-Reinforced Polymer Composites