Compacting and Sintering Behavior of Nano ZrO 2 Powders

W Li,L Gao

DOI: https://doi.org/10.1016/s1359-6462(01)00753-9

IF: 6.302

2001-01-01

Scripta Materialia

Abstract:The compacting and sintering behavior of nano ZrO2(3Y) powder synthesized by a new method which called heating of alcohol-aqueous salt solutions were investigated. It was found that the density of the green compact was increased with calcining temperature of the powder. The green compact obtained at 450MPa was translucent which means the structure was uniform and the pores were small and narrow distributed. The powder calcined at 450°C had a better sintering behavior than those calcined at lower or higher temperatures because of its smaller hard agglomerates. A relative density of 98.5% could be obtained when the powder was sintered at 1150°C for 2h. Different with the classic sintering theory which believes that the grain grows rapidly during the final sintering stage, it was found that the grain grew slowly even when the sintering temperature was 1150–1300°C high and the relative density of Y-TZP materials was higher than 98%. This new phenomenon was explained by the enrichment of Y+ on the grain boundaries which hindered the grain growth.