Abstract:Currently, the hot forming of aluminum alloys has garnered significant attention for overcoming poor formability at room temperature (RT). However, the current hot forming technique is facing problems such as time-consuming procedures and high economic cost. To improve forming efficiency, we herein propose a novel forming technique for heat-treatable aluminum alloys, termed pre-aged hardening warm forming (PHF) process. An Al–Zn–Mg–Cu alloy is used to investigate the flow behavior, drawing formability, and post-forming mechanical properties during the aforementioned process. Uniaxial tensile tests and Erichsen tests are conducted to evaluate the plastic flow behavior and drawability, respectively. Stamping tests are performed on a cap beam component to verify the engineering feasibility of the forming technique. Optical microscopy (OM) and transmission electron microscopy (TEM) are performed to characterize the microstructure evolution during the PHF process. The tensile test results show that the pre-aged alloys exhibit true fracture elongation similar to the fracture elongation of the O-temper alloy at RT, and that the Erichsen values of the pre-aged alloys are 5%–16% higher than that of the O-temper alloy at 200 °C. The results of the stamping tests for the cap beam component indicate that the optimal final strength of the stamped component achieves σ/σ0.2 = 566 MPa/500 MPa, exceeding the strength of the AA7075-T6 alloy. OM observations show that the stamping process does not significantly affect the grain sizes of the pre-aged alloys. TEM results show that numerous thermostable GPⅡ zones exist in the pre-aged alloys, and that the stamping procedure transforms the GPⅡ zones to dispersed η′ phases and results in the entanglement of numerous dislocations. The dual effects of phase transformation and plastic deformation during the PHF process contribute to the desirable mechanical properties of the stamped components.

Research on Synchronized Cooling Hot Forming Process of 6016 Aluminum Alloy

Numerical Investigation for Formability of Aluminum 6016 Alloy under Non-Isothermal Warm Forming Process

Experimental and Numerical Simulation Analytical Studies for Forming Limit of 2024 Aluminum Alloy on Synchronous Cooling Hot Sheet Metal Forming

Experimental and Numerical Investigation on Strengthening Behavior of 7075 Aluminum Alloy Sheets in Hot Forming–Quenching Integrated Process

Experimental Investigation on Hot Forming–quenching Integrated Process of 6A02 Aluminum Alloy Sheet

Strengthening Behavior of Al–Cu–Mg Alloy Sheet in Hot Forming–quenching Integrated Process with Cold–hot Dies

Comparative study on deformation behavior, microstructure evolution and post-forming property of an Al Zn Mg Cu alloy in a novel warm forming process

Study on process parameters optimization of 7075-T6 aluminum alloy under contact heating

Microstructure and mechanical properties of 6082 aluminum alloy processed by preaging and hot forging

Construction of 6061-T6 aluminum alloy constitutive model based on hot bulging test and study on the non-isothermal hydroforming process

Investigation on effect of high-efficiency solid solution and hot stamping process on microstructure evolution and mechanical properties of high-strength aluminum alloy

Microstructural Evolution and Mechanical Properties of 6082 Aluminum Alloy Automotive Rear Swing Arm Produced by Integrated Process

Research on the effect of temperature increase during flow forming without cooling on 6060 aluminum alloy

Hot Forming-Quenching Integrated Process with Cold-Hot Dies for 2a12 Aluminum Alloy Sheet

Thermal constitutive model and numerical simulation of hot forming for 6061-T6 aluminum alloy

Microstructural evolutions and mechanical properties of 6082 aluminum alloy part produced by a solution-forging integrated process

Investigation of formability, microstructures and post-forming mechanical properties of heat-treatable aluminum alloys subjected to pre-aged hardening warm forming

The Effect of Hot Forming–Quenching and Heat Treatment Processes on the Mechanical Properties of AA6016 Aluminum Alloy Sheets

Investigation on Warm/hot Hydro-Forming of High Strength Aluminum Alloy Sheet

Modeling mechanical properties and plastic strain for hot forming-quenching AA6061 aluminum alloy parts

Strength and Formability Improvement of Al-Cu-Mn Aluminum Alloy Complex Parts by Thermomechanical Treatment with Sheet Hydroforming