Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Preparation of Activated Carbon with Low-ash Content from Sawdust and the Recovery of Activating Agent

Biomass-Based Activated Carbon and Activators: Preparation of Activated Carbon from Corncob by Chemical Activation with Biomass Pyrolysis Liquids

Pre-Treatment Methods for Regeneration of Spent Activated Carbon

Preparation of Activated Carbon from Co-Pyrolysis Activation of Fly Ash and Biomass

Study on activated carbon production from hydrolysate of sawdust

Preparation of Activated Carbon from Pyrolyzed Rice Husk by Leaching out Ash Content after CO2 Activation

Efficient preparation of carbon nanospheres-anchored porous carbon materials and the investigation on pretreatment methods

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Activated carbon from biomass precursors using phosphoric acid: A review

&Amp;lt;i&gt;microwave-Assisted Carbonization of Phosphoric Acid Activated Biomass&lt;/i&gt;

Optimization of Preparation of Hazelnut Shell Activated Carbon and Characterization

Effect of Co-solution of Carbon Precursor and Activating Agent on the Textural Properties of Highly Porous Activated Carbon Obtained by Chemical Activation of Lignin With H3PO4

Preparation of Activated Carbons from Wet Activated Sludge by Direct Chemical Activation.

Effect of Na 2 CO 3 , HF, and CO 2 Treatment on the Regeneration of Exhausted Activated Carbon Used in Sintering Flue Gas

Effects of the heating history of impregnated lignocellulosic material on pore development during phosphoric acid activation

Optimized preparation of activated carbon with high porosities based on puck shells (Afrostyrax lepidophyllus) by response surface methodology and physico-chemical characterization

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

Methods for preparation and activation of activated carbon: a review

Real-time monitoring the carbonization and activation process of activated carbon prepared from Chinese parasol via zinc chloride activation

Preparation of Activated Carbons with Phosphoric Acid Method from Walnut Hull and Its Application in Brewery Wastewater Treatment

Preparation of activated carbon from waste cation exchange resin and its application in wastewater treatment