Formation Mechanism and Structure Evolution of Austenitic Stainless Steel 304 during Solidification with Near-Rapid Rates

Shen Lijuan,Xing Shuqing,Ma Yonglin,Bai Liang,Li Defa,Li Jianfei
DOI: https://doi.org/10.3969/j.issn.1003-8620.2012.04.016
2012-01-01
Abstract:The effect of Cr_(eq)/Ni_(eq) and cooling rate(1.5~1 000℃/s) on structure morphology and distribution of ascast solidification structure of austenite stainless steel 304(/%:0.053C,0.55Si,1.50Mn,0.030P,0.002S,17.02Cr, 8.01 Ni,0.50Cu,0.08 Mo) is studied by induction furnace melting the steel and direct-casting on a water-cooling copper mold to get a sample with 7 mm thickness and 25 mm diameter.Results show that with increasing cooling rate to 75~90℃/s,the primary solidification mode of steel transferred from FA(ferrite-austenite) mode to AF(austenite-ferrite) mode, the primary phase is modified from dendritic ferrite to dendritic austenite,as the cooling rate is~1 000℃/s,the blocky ferrite structure is observed,and the dendritic austenite is replaced by cellular austenite.
What problem does this paper attempt to address?