Abstract:Abstract We are reporting the effect of thickness on the Seebeck coefficient, electrical conductivity and power factor of Ca 3 Co 4 O 9 thin films grown on single-crystal Sapphire (0001) substrate. Pulsed laser deposition (PLD) technique was employed to deposit Ca 3 Co 4 O 9 films with precisely controlled thickness values ranging from 15 to 75 nm. Structural characterization performed by scanning electron microscopy (SEM) and atomic force microscopy (AFM) showed that the growth of Ca 3 Co 4 O 9 on Sapphire (0001) follows the island growth-mode. It was observed that in-plane grain sizes decrease from 126 to 31 nm as the thickness of the films decreases from 75 to 15 nm. The thermoelectric power measurements showed an overall increase in the value of the Seebeck coefficient as the films’ thickness decreased. The above increase in the Seebeck coefficient was accompanied with a simultaneous decrease in the electrical conductivity of the thinner films due to enhanced scattering of the charge carriers at the grain boundaries. Because of the competing mechanisms of the thickness dependence of Seebeck coefficient and electrical conductivity, the power factor of the films showed a non-monotonous functional dependence on thickness. The films with the intermediate thickness (60 nm) showed the highest power factor (~ 0.27 mW/m-K 2 at 720 K).

Growth and Laser Induced Thermoelectric Voltages Effect of the c-Axis Oriented Thermoelectric Ca3Co4O9 Thin Films on Sapphire Substrates

Understanding the effect of thickness on the thermoelectric properties of Ca3Co4O9 thin films

Synthesis of the thermoelectric thin films of Ca 3Co 4O 9 and Ca 3Co 2O 6 using pulsed-laser deposition techniques

Preparation and Laser-Induced Thermoelectric Voltage Effect of Bi2Sr2Co2Oy Thin Films Grown on Al2O3 (0001) Substrate

Synthesis of the Thermoelectric Thin Films of Ca3Co4O9 and Ca3Co2O6 Using Pulsed-Laser Deposition Techniques

Intrinsically Modified Thermoelectric Performance of Alkaline-Earth Isovalently Substituted [bi2ae2o4][coo2]y Single Crystals

Study on the Thermoelectric Thin Films of Ca_3Co_4O_9 Using Pulsed-laser Deposition Techniques

Preparation of Single-Phase Nd1.85 Ce0.15 CuO4 Thin Films by Pulse Laser Deposition and the Laser-Induced Thermoelectric Voltage Effect

Transverse laser induced thermoelectric voltage effect in tilted La0.5Sr0.5CoO3 thin films

Effects of Crystallinity on Laser-Induced Voltage Effect from Zn0.9Co0.1O Thin Film

Laser Induced Thermoelectric Voltage of Atomic Layer Thermopile Materials

Temperature Stability of Laser Induced Thermoelectric Voltage Signal in Colossal Magneto Resistance Thin Films

The Structure and Laser-Induced Thermoelectric Effect on Tilt Orientation Tlbacacuo Films

Time Dependence of Laser-Induced Thermoelectric Voltages in La1−xCaxMnO3 and YBa2Cu3O7−δ Thin Films

Development of a transverse thermoelectric voltage effect in artificial SrTiO3/SrTi1−xNbxO3 epitaxial multilayer films with incline-oriented sublayers

Efficient preparation of the inclined La<sub>1-x</sub>Ca<sub>x</sub>MnO<sub>3</sub> films with excellent light-induced transverse thermoelectric performance based on MOCVD process

Transverse Laser-Induced Thermoelectric Voltages in Tilted La2−xSrxCuO4 Thin Films

Laser-induced Transverse Voltage in (111)-Oriented TiO1+δ Epitaxial Thin Films with Cubic Structure

Facile and time-resolved chemical growth of nanoporous CaxCoO2 thin films for flexible and thermoelectric applications

Efficient preparation of the inclined La1-xCaxMnO3 films with excellent light-induced transverse thermoelectric performance based on MOCVD process

Influence of annealing oxygen pressure on the laser-induced thermoelectric voltage effect in YBa2Cu3O7-x thin films