Abstract:Gas metal arc welding (GMAW) of aluminum alloys has recently become popular in the auto industry to increase fuel efficiency of a vehicle. In many situations, the weld is short (say, less than two inches) and the “end effects” become very critical in determining the strength of the weld. At the beginning stage of the welding, when the metal is still “cold”, which is frequently called cold weld, limited weld penetration occurs. On the other hand, at the ending stage of the welding, a “crater” is formed involving micro-cracks and micro-pores. Both the cold weld and the crater can significantly decrease the strength of the weld and are more severe for aluminum alloys as compared to steels. Hence, there are strong needs to improve the GMAW process in order to reduce or eliminate the aforementioned end effects. In this paper, both mathematical modeling and experiments have been conducted to study the beginning stage, ending stage, as well as the quasi-steady-state stage of GMA welding of aluminum alloys. In the modeling, a three-dimensional model using the volume-of-fluid (VOF) method is employed to handle the free surfaces associated with the impingement of droplets into the weld pool and the weld pool dynamics. Transient weld pool shapes and the distributions of temperature and velocity in the weld pool are calculated. The predicted solidified weld bead shapes, including weld penetration and/or reinforcement, are in agreement with experimental results for welds in the aforementioned three stages. It was found that the thickness of the molten weld pool is smaller and there is no vortex developed, as compared to steel welding. The lack of penetration in cold weld is due to the lack of pre-heating by the welding arc. Three techniques are proposed and validated numerically to improve weld penetration by increasing the energy input at the beginning stage of the welding. The crater formation is caused by rapid solidification of the weld pool when the welding arc is terminated. By reducing welding current and reversing the welding direction before terminating the arc, the weld pool is maintained “hot” for a longer time allowing melt flow to fill-up the crater. This method is validated experimentally and numerically to be able to eliminate the formation of the crater and the associated micro-cracks.

Formation of Weld Crater in GMAW of Aluminum Alloys

Transport Phenomena and Their Effect on Weld Quality in GMA Welding of Aluminum Alloys

Numerical Modeling of Cold Weld Formation and Improvement in Gmaw of Aluminum Alloys

Three-Dimensional Modeling Of Gas Metal Arc Welding Of Aluminum Alloys

Molten pool behaviors and their influences on welding defects in narrow gap GMAW of 5083 Al-alloy

Study on Root Hump Formation Mechanism in Full Penetration Laser Welding with Backing Gas for Aluminum Alloy

Investigation of Microstructure and Hot Crack Formation Mechanisms in the Heat-Affected Zone of GTAW-Repaired Cast K4002 Nickel-Based Superalloy with HGH3113 Filler Metal

Numerical Simulation and Weld Morphology of 5056 Aluminum Alloy TIG Welding

Numerical Simulation of Keyhole Morphology and Molten Pool Flow Behavior in Aluminum Alloy Electron-Beam Welding

Modeling of transport phenomena and solidification cracking in laser spot bead-on-plate welding of AA6063-T6 alloy. Part II—simulation results and experimental validation

Effect of Swing Arc on Molten Pool Behaviors in Narrow-Gap GMAW of 5083 Al-alloy

Effect of Molten Pool Behaviors on Welding Defects in Tandem NG-GMAW Based on CFD Simulation

Research on Welding Process of Casting Aluminum Alloy Front Auxiliary Cradle

An Improved Model of Porosity Formation During Pulsed GTA Welding of Aluminum Alloys

Numerical simulation on molten pool behavior of narrow gap gas tungsten arc welding

Numerical Modeling of Welding Porosity Formation and Dendrite Growth of 6xxx Aluminum Alloys

Molten Pool Behaviors in Double-Sided Pulsed GMAW of T-Joint: A Numerical Study

Weld Pool Dynamics and the Formation of Ripples in 3d Gas Metal Arc Welding

Study of Weld Formation in Swing Arc Narrow Gap Vertical GMA Welding by Numerical Modeling and Experiment

Numerical Investigation on Molten Pool Dynamics and Defect Formation in Electron Beam Welding of Aluminum Alloy

Numerical Simulation of Tungsten Inert Gas Welding of 5A12 Aluminum Alloy Limited Size Sheet