Abstract:Crystalline microporous aluminophosphates with AFI-type structure have been hydrothermally synthesized by the use of low-cost and biological template of tetramethylguanidine (TMG), which were characterized by X-ray powder diffraction (XRD), scanning electron micrograph (SEM), nitrogen isotherms, infrared, elemental analysis, thermogravimetry (TG), temperature-programmed desorption of NH3 (TPD-NH3), and photoluminescent (PL) techniques. XRD experiments show that TMG-templated synthesis has high crystallization rate, compared with conventional organic template of triethylamine. Observation of SEM images indicates that the crystalline aluminophosphate products are spheres ranged in 5–30μm. The results obtained from nitrogen isotherms show that these spherical particles of AlPO-5 crystals have mesoporosity, which are due to the presence of intercrystalline voids. The formation of hierarchical mesoporous and microporous crystalline spheres would be favorable for mass transport in catalysis and adsorption, compared with the small and sole microporous crystals. The combination of infrared, TG, and elemental analysis indicates that there are about 1.4 TMG molecules per unit cell of AlPO-5. Furthermore, TMG-templated synthesis are extended to prepare heteroatom-substituted AlPO-5 crystals such as SAPO-5, MnAPO-5, and CoAPO-5, and acidic measurements of TPD-NH3 show the order of sample acidity is as follows: CoAPO-5>MnAPO-5>SAPO-5≫AlPO-5. The determination of PL shows that as-synthesized AlPO-5 templated by TMG has 38 nm red-shift for emission peak, compared with TMG liquid. Importantly, in this work, the use of TMG might open a door to use the guanidine-type compounds as templates for “green” preparation of aluminophosphate-based microporous crystals in the future.

Microemulsion-based Solvothermal Synthesis of Aluminium Orthophosphate Nanocrystals

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Low-Temperature Synthesis and Characterization of AlPO-Cristobalite in Ionic Liquid

Multinuclear solid-state NMR studies on the formation mechanism of aluminophosphate molecular sieves in ionic liquids

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Synthesis and crystal morphology control of AlPO4-5 molecular sieves by microwave irradiation

α-Calcium Sulfate Hemihydrate Nanorods Synthesis: A Method for Nanoparticle Preparation by Mesocrystallization

Solid-State Synthesis of Aluminophosphate Zeotypes by Calcination of Amorphous Precursors

Microwave preparation of molecular sieve AlPO4-5 with nanometer sizes

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study

Size-controlled synthesis of nano α-alumina particles through the sol–gel method

Synthesis of Al(OH)3Nanostructures from Al(OH)3Microagglomerates Via Dissolution-Precipitation Route

Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds

An Experimental Study on the Shape Changes of TiO2 Nanocrystals Synthesized by Microemulsion-Solvothermal Method

Synthesis of Aluminophosphate Molecular Sieves in Alkaline Media

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Synthesis of Nanosized Pseudoboehmite and γ-Al2O3 by Control Precipitation Method

Microwave-Assisted Solvothermal Synthesis of AlOOH Hierarchically Nanostructured Microspheres and Their Transformation to Γ-Al2o3 with Similar Morphologies

Tetramethylguanidine-templated Synthesis of Aluminophosphate-Based Microporous Crystals with AFI-type Structure

Synthesis of Nanosized Pseudoboehmite and γ-Al<sub>2</sub>O<sub>3</sub> by Control Precipitation Method