Abstract:Piezoelectric devices based on high-temperature stable single crystals are of increasing interest due to a wide range of potential applications, such as actuators and resonant gravimetric sensors. The latter require highly accurate resonant-frequency measurements at temperatures as high as 1000 °C, and this can only be achieved with narrow resonance peaks and correspondingly low acoustic loss at these temperatures. Relevant atomistic defects in langasite (La 3 Ga 5 SiO 14 , LGS) and catangasite (Ca 3 TaGa 3 Si 2 O 14 , CTGS) are reviewed with respect to their impact on electrical conductivity and acoustic loss. The focus on these crystals also enables a comparison of electroacoustic properties of partially disordered (LGS) and ordered (CTGS) crystals and the formulation of approaches for reducing acoustic loss and enhancing device performance. Starting with defect chemistry models for LGS and CTGS, electrical conductivities as a function of temperature and oxygen partial pressure are considered. One result of this analysis is that contributions of oxygen ions to the total conductivity are determined to be relatively small in the studied crystals. Temperature-dependent acoustic loss of LGS and CTGS crystals is also studied. Two independent techniques, contact resonant piezoelectric spectroscopy, and a contactless tone-burst excitation technique, are applied. Contributions to the measured acoustic loss are determined by fitting loss-related functions for point defects and conductivity-related relaxations. The extracted fit parameters, in particular the activation energies of the processes, are discussed and compared with that of the electrical conductivity. The losses are caused by a superposition of several mechanisms including conductivity-related relaxations, point-defect relaxations and intrinsic phonon-phonon loss. The long-term stability of the crystals is also evaluated at 1000 °C with respect to fundamental materials properties including electrical conductivity and resonant frequency. After one year of thermal treatment, the resonance frequency of CTGS resonators from different crystal sources is found to decrease by no more than 0.4 %. Thus, the applicability of CTGS as a piezoelectric resonator that operates for long periods at extreme temperatures, such as a resonant nanobalance, is demonstrated. Application examples to be presented include resonant nanobalances for in-situ monitoring of non-stoichiometry and phase transformations in thin films during growth at high temperatures. In this context, the key application properties of the sensors at high temperatures, such as mass sensitivity and resolution, are discussed. As an application example, the attached figure shows the oxygen non-stoichiometry x of thin praseodymium-cerium oxide films (Pr 0.1 Ce 0.9 O 2-x ) at 700 °C as a function of oxygen partial pressure determined by LGS and CTGS nanobalances, which agrees very well with literature data (chemical capacitance: D. Chen et al., Chem. Mater. 2014, 26, 22, 6622–6627). Figure 1

Growth and Characterization of Piezoelectric Sr3Ga2Ge4O14 Crystals.

Piezoelectric properties of (Sr 0.2 Ca 0.8 ) 3 TaGa 3 Si 2 O 14 and Ca 3 TaGa 3 Si 2 O 14 single crystals grown via vertical Bridgman method

Characterization of high temperature piezoelectric crystals with an ordered langasite structure

Crystal Growth, Characterization, and Properties of Nonlinear Optical Crystals of Li x Ag 1- x GaSe 2 for Mid-Infrared Applications

Growth of large langatate (La3Ta0.5Ga5.5O14, LTG) crystals with high electrical resistivity

Crystallization of GeO2 thin films into alpha-quartz: from spherulites to single crystals

Growth and Characterization of Si-doped GaAs Crystals for LED Application

Vertical Bridgman Growth and Characterization of Large ZnGeP2 Single Crystals

High-Temperature Piezoelectric Resonators: Electroacoustic Properties and Applications of Langasite-Type Crystals

Large-sized crystal growth and piezoelectric properties of the single crystals of LiNa 5 Mo 9 O 30

Crystal Growth, Characterization, and Properties of Nonlinear Optical Crystals of Li 0.5 Ag 0.5 GaTe 2 for Mid-Infrared Applications

Langasite as Piezoelectric Substrate for Sensors in Harsh Environments: Investigation of Surface Degradation under High-Temperature Air Atmosphere

Piezoelectricity in wide bandgap semiconductor 2D crystal GaN nanosheets

2 in. Bulk β-Ga2O3 Single Crystals Grown by EFG Method with High Wafer-Scale Quality

Growth of Large Size AgGaGeS 4 Crystal for Infrared Conversion

Study on the Growth of Pure and Ga3+ Doped γ-LiAlO2 Crystals

Improved Extraction of Second-Order Material Constants for Current Generation Y-Grown La₃Ga5.5Nb0.5O₁₄ (LGN) Crystal

Pressure-Assisted Method for the Preparations of High-Quality AaGaS2 and AgGaGeS4 Crystals for Mid-Infrared Laser Applications

Growth, structure and electrical properties of aluminum substituted langasite family crystals

Growth and Characterization of Novel Piezo-/Ferroelectric Single Crystals from the PSN-BS-PT Ternary System