Abstract:In order to achieve well-performing chemical strengthening behavior, the composition of 86.12(xSiO(2)-yAl(2)O(3)-zP(2)O(5))- 9.95Na(2)O- 1.27ZnO- 2.66Li(2)O (x = 55-85wt%, y = 10-40wt% and z = 5-35wt%) were prepared by conventional melt-quenching technique. The glass forming region was obtained. Two compositional series of 65SiO(2)-yAl(2)O(3)-zP(2)O(5) (15 <= y <= 30, 5 <= z <= 30, 5 <= z <= 20) (Series I) and xSiO(2)-20%Al2O3-zP(2)O(5) (60 <= x <= 75, 5 <= z <= 20) (Series II) have been investigated. The relationship between glass structure and composition was investigated. The results show that the transparent and homogeneous glass is formed when the glass former P2O5 is lower than or equal to 15 wt% roughly. The P2O5 substitution for Al2O3 accelerates the depolymerization of aluminosilicate network. Phosphorus acts as network formers in the form of P-1 and P-2 units. In the case of the P2O5 substitution for SiO2, the roles of phosphorus in the glass network include P-0, P-1, P-2 and P-3 units. Furthermore, the Series I and Series II glass samples were chemical strengthened. The ion-exchange depth and the elastic modulus before and after chemical strengthening were studied. The results reveal that the ion exchange depth and elasticity modulus after chemical strengthening is maximum at 64 mu m and 80.5 GPa for x/z = 5.4 sample, respectively. The addition of phosphorus accelerates ion exchange, which is mainly attributed to the formation of ion channels. The number of P-n and the coordination number of phosphorus are the main factors effecting the ion channels.

The Influence of Sb<sub>2</sub>O<sub>3</sub> Addition on the Properties of Low-melting ZnO–P<sub>2</sub>O<sub>5</sub> Glasses

Fabrication and properties of novel low-melting glasses in the ternary system ZnO–Sb2O3–P2O5

Effect of R_2O on the Properties of ZnO-Sb_2O_3-P_2O_5 Low-melting Glasses

Effects of Additives on the Thermal Properties of Low Melting Point Lead Borosilicate Glasses

Effect Of Sb2o3 On Thermal Properties Of Glasses In Bi2o3-B2o3-Sio2 System

Low Melting Pbo-Zno-P2o5 Glasses

Effect of Bi2O3 content on the structure and properties of Bi2O3-B2O3-BaO-ZnO glass

Influences of La2O3 on the Structure and Properties of 50p2o5–30sb2o3–10cao–5al2o3–5teo2 Low-Melting Glasses

The Role of Phosphate in the Glass Forming Region, Structure and Mechanical Properties for the SiO2-Al2O3-P2O5 System Contains High-Aluminum

Influence of Li2O–B2O3–SiO2 Glass on the Sintering Behavior and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO2 Ceramics

FTIR and XPS studies of low-melting PbO-ZnO-P2O2 glasses

Bond characteristics, microstructure, and microwave dielectric properties of Bi2O3–ZnO–B2O3 glass-ceramics with Li2O substitution

La2O3 Substitution in Li-Al-P-O-N Glasses for Potential Solid Electrolytes Applications

Effect of SrO Content on Microstructure of Bi2O3-B2O3-ZnO-BaO-SrO Low-Melting Glass Frit and Joining Performance of Sodalime Glass Substrates

Effects Of Oxidizing Additives On Optical Properties Of Bi2o3-B2o3-Sio2 Glasses

Effects of ZnO on Crystallization, Microstructures and Properties of BaO–Al2O3–B2O3–SiO2 Glass–ceramics

Effects of Li2O-B2O3-SiO2 glass on the low-temperature sintering of Zn0.15Nb0.3Ti0.55O2 ceramics

Effect of ZnO content on structure and properties in high refractive index BaO-ZnO-TiO2-SiO2 glass system

Effects of Oxidizing Additives on Optical Properties of Bi2O3–B2O3–SiO2 Glasses

Impact of the La2O3 Addition on the Structure, Mechanical and Radiation Attenuation Features of La2O3–ZnO–SiO2–B2O3 Glass

Network structure, crystallization behavior, and microwave dielectric properties of ZnO-B2O3 glass-ceramics with ZrO2 additions