Influence of Boron on Microstructure and Mechani cal Properties of Abrasive Wear Resistant Ductile Cast Iron
ZHAO Ai-min,MAO Wei-min,SUN Feng,ZHEN Zi-sheng,ZHONG Xue-you,MA Zhen-sheng
DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.2001.01.014
2001-01-01
Journal of Iron and Steel Research International
Abstract:The influence of boron on micros tructure and mechanical properties of ductile cast iron with C 3.4 %～3.8 %, Si 2.0 %～3.0 % and Mn 2.0 %～3.0 % has been studied.The results indicated that th e amount of the carbide in the as cast microstructure increases as the boron con tent increases.At the same time, the hardness rises and the impact toughness de clines.When boron content surpasses 0.010 %, there is some clear continuous car bide network or discontinuous carbide network in the microstructure, as a result , the impact toughness declines greatly.After heat treated by quenching and tem pering, the carbide in the cast microstructure decomposes more or less.When the boron content is controlled between 0.003 % and 0.010 %, the carbide in the hea t-treated samples generally disappears, and the hardness keeps about HRC 50, an d the impact toughness comes up to or surpasses 9 J/cm2.However, when boron c ontent surpasses 0.010 %, some discontinuous carbide network or carbide blocks e xist, thus the hardness rises slightly, at the same time, the impact toughness declines obviously.