Effect of TiO_2 addition on zirconia-mullite composites fabricated by in-situ controlled crystallization of Si-Al-Zr-O amorphous bulk

LIANG Shu-quan,LIU Rong,TAN Xiao-ping,GUAN Di-kai

DOI: https://doi.org/10.1007/s11771-011-0840-1

2011-01-01

Abstract:Zirconia-mullite composite ceramics were fabricated by in-situ controlled crystallization of Si-Al-Zr-O amorphous bulk. The effects of TiO 2 addition on the fabrication of zirconia-mullite composites were investigated. The ultra-fine zirconia-mullite composite ceramics were prepared from the amorphous bulk treated at 980 °C for nucleation and 1 140 °C for crystallization. The phase transformation of the ceramics was examined using differential scanning calorimetry (DSC) and X-ray diffractometry (XRD). The microstructural features of the samples were evaluated with scanning electron microscopy (SEM), energy dispersive spectroscopy (EDX) and transmission electron microscopy (TEM). The mechanical properties were also determined using Vickers indentation. The results show that the TiO 2 additives with mass fraction of 1%-7% reduce the formation temperature of t-ZrO 2 and mullite. When the mass fraction of TiO 2 additives is less than 5%, the phases do not change, and most of TiO 2 dissolves in ZrO 2. When the mass fraction of TiO 2 additives is over 5%, the excessive TiO 2 forms a new phase, ZrTiO 4. Meanwhile, the results also show that TiO 2 additives have a great impact on the microstructure and mechanical properties of zirconia-mullite composites. As the TiO 2 content increases from 1% to 7% (mass fraction), the grain size and the Vickers hardness of zirconia-mullite composites increase. The composite with 3% (mass fraction) TiO 2 additives attains relatively higher fracture toughness. © Central South University Press and Springer-Verlag Berlin Heidelberg 2011.