Influence of V substitutions on sintering behaviors and microwave dielectric properties of Ba4LiNb3O12 ceramic
Yulong Tian,Wei Wang,Xin Wang,Jie Li,Di Zhou
DOI: https://doi.org/10.1111/jace.20183
IF: 4.186
2024-10-03
Journal of the American Ceramic Society
Abstract:In this study, a series of Ba4Li(Nb1‐xVx)3O12 (x = 0.05∼0.3) ceramics were synthesized using the solid‐state reaction method. X‐ray powder diffraction (XRD) analysis shows that the composite ceramics contain both Ba4LiNb3O12 and Ba3(VO4)2 phases, without any other phases present. The grains consist of Ba4LiNb3O12 and Ba3(VO4)2, as illustrated by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Additionally, with the increase of V content, the grain size decreases, and the εr (microwave dielectric constant) decreases, the τf (resonant frequency temperature coefficient) value decreases, and the Q×f value increases (where Q = quality factor = 1 / dielectric loss, and f = resonant frequency). The densest Ba4Li(Nb0.7V0.3)3O12, with a εr of 31.3, τf of + 70 ppm/°C, and high Q×f of 42 850 GHz, was obtained at a sintering temperature of 1350°C. Furthermore, the addition of 5 wt.% BaCu(B2O5) (BCB) into Ba4Li(Nb0.7V0.3)3O12 resulted in obtaining dense ceramics at a sintering temperature of 925°C, with a εr of 23.5, a high Q×f value of 14 370 GHz, and τf of + 88 ppm/°C. Further investigations have shown that Ba4Li(Nb1‐xVx)3O12 ceramics are chemically compatible with Ag, suggesting its potential use in low‐temperature cofired ceramics technology.
materials science, ceramics