EFFECTS OF SrO OR SnO2 ADDITION ON THE DIELECTRIC PROPERTIES OF Ba4.5(Nd0.84, Bi0.16)9 Ti18O54 MICROWAVE CERAMICS

石勇,靳正国,程志捷,魏学忠,徐廷献

DOI: https://doi.org/10.3321/j.issn:0454-5648.2003.06.010

2003-01-01

Abstract:The microwave dielectric properties and microstructure of Ba 4.5(Nd 0.84,Bi 0.16) 9Ti 18O 54(BNBT) ceramics with SrO or SnO 2 additives were investigated. BNBT precursor powders doped with different contents of SrCO 3or SnO 2 for the substitution of Ba or Ti were synthesized at 1 100 ℃ for 3h and then BNBT samples were sintered at 1 270 ℃ for 3 h. The dielectric constant e r and the quality factors Q were measured at 10 GHz by using resonance cavity method and the temperature coefficients of resonant frequency were also measured in the temperature range of 20-90 ℃. Experimental results indicate that the substitution of 0.04 mol Sr ions for Ba ions can improve Qf values from 5 899 GHz to 9 259 GHz and keep high dielectric constant. It is explained that the substitution reduces the inner strain, which is caused by the larger Ba ions occupying the sites in the perovskite blocks for Nd ions, because the ionic radius of the Sr ion is smaller than that of the Ba ion. The doping with small amount of Sn is helpful to decrease τ f from 28.7×10 -6/K to 13.5×10 -6/K and improve dielectric constant by substitution of Sn ion for Ti ion at the site of Ti-O octahedral, which results in the increase of cell volume of the tungsten bronze-type structure.