Abstract:In this work, microstructure and texture evolution in the sheets of Mg alloy AZ31 was studied by means of bidirectional cyclic in-plane bending at 423 K followed by annealing at 523 K. The deformed and subsequent annealed microstructures were investigated by OM and SEM/EBSD examinations. The results showed that twinning is the dominant deformation mechanism. With the increase of deformation pass, more and more twins were produced in the grains near the surfaces of the sheets and finally these grains were serially divided up by twinning intersections. But only a few twins were formed in the grains of the middle of the sheets due to relatively lower strain. Finally, a gradient structure with high-density twins in the regions near the surfaces and, in contrast, lower density ones in the center of the sheets were induced. After 6 pass bending at 423 K followed by a subsequent annealing at 523 K, the average grain size near the surfaces was reduced to about 10 mu m from the original size of 46 mu m due to operation of static recrystallization at twin intersections and compression twins. Particularly, the relative intensity of the strong texture developed in the sheets was severely weakened by repeated bending, and this led to an increase of fracture elongation from 19.01% to about 24% with little change of tensile strength.

Tensile Properties and Microstructure of AZ31B Magnesium Alloy Sheet Processed by Repeated Unidirectional Bending

Structure and Properties of Az31b Magnesium Alloy Sheets Processed by Repeatedly Unidirectional Bending at Different Temperatures

Texture Evolution and Mechanical Properties of AZ31B Magnesium Alloy Sheets Processed by Repeated Unidirectional Bending

Textural Evolution of AZ31B Magnesium Alloy Sheets Undergoing Repeated Unidirectional Bending at Room Temperature

Influence of Microstructure and Texture on Formability of AZ31B Magnesium Alloy Sheets

Enhancement of Tensile Ductility and Stretch Formability of AZ31 Magnesium Alloy Sheet Processed by Cross-Wavy Bending

Microstructure Evolution and Mechanical Behavior of AZ31 Magnesium Alloy Sheet with Bimodal Texture under Bending Deformation

Effect of Multi-Pass Bending Deformation on Microstructure Evolution and Mechanical Properties of AZ31 Alloy Sheet

Influence of Initial Texture on Formability of AZ31B Magnesium Alloy Sheets at Different Temperatures

Enhanced Mechanical Properties of AZ31 Magnesium Alloy Sheets by Continuous Bending Process after V-bending

Microstructures and tensile properties of commercial AZ31B magnesium alloy sheets

Enhanced Mechanical Properties of AZ31B Magnesium Alloy Thin Sheets Processed by On-Line Heating Rolling

Microstructural and Textural Evolution of Az61 Magnesium Alloy Sheet During Bidirectional Cyclic Bending

Structure Evolution of Az31 Mg Alloy Sheet During Bidirectional Cyclic Bending at Low Temperature and Subsequent Annealing

Cold stamping formability of AZ31B magnesium alloy sheet undergoing repeated unidirectional bending process

Microstructure and Formability Evolutions of AZ31 Magnesium Alloy Sheets Undergoing Continuous Bending Process

Texture Weakening of AZ31 Magnesium Alloy Sheet Obtained by a Combination of Bidirectional Cyclic Bending at Low Temperature and Static Recrystallization

Forming limit of textured AZ31B magnesium alloy sheet at different temperatures

Microstructures and Mechanical Properties of Roll-casting AZ31B Magnesium Alloy Sheet

Influence of Continuous Bending Process on Texture Evolution and Mechanical Properties of AZ31 Magnesium Alloy

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling