Abstract:The nanocubic Co3O4 was synthesized by hydrothermal oxidation method. The effects of cobalt salt, precipitating agent, surfactant, solvent, pH value of the suspension and the amount of oxidant H2O2 on the morphology and structure of Co3O4 were investigated. The Co3O4 powders were characterized by transmission electron microscope and X-ray diffraction. The results show that the morphology of Co3O4 is closely dependant on the anion in cobalt salts, but it is not so sensitive to the precipitating agents and solvents. The amount of H2O2 is the key factor to obtain Co3O4 with spinel crystal structure. The optimum synthetic conditions of uniform shape-controlled Co3O4 nanocubes are as follows: Co(CH3COO)2 · 4H2O as cobalt salt, KOH as precipitating agent, polyethylene glycol with relative molecular mass of about 20000 as surfactant, water-n-butanol as solvent system, pH value of 8–9, the molar ratio of H2O2 to Co2+ above 2.5:1.0, hydrothermal temperature of 160 °C and hydrothermal holding time of 10 h. The tap density and apparent density of nanocubic Co3O4 obtained with the average particle size of 20 nm are 1.01 g/cm3 and 0.70 g/cm3, respectively.

Mechanochemical Synthesis of Cobalt Oxide Nanoparticles

Solid-state Synthesis of Cobalt Oxide (co3 O4 ) Nanocrystallites and Crystallization Kinetics During Thermal Treatment

Mechanochemical Route to Synthesize Co 3 O 4 /cuo Composite Nanopowders

Preparation of CdO Nanoparticles by Mechanochemical Reaction

Mechanochemical Synthesis of In2O3/CuO Nanocomposites

Synthesis of Co3O4 nanoparticles via an ionic liquid-assisted methodology at room temperature

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Hydrothermal Synthesis of Mesoporous Co3O4 Nanobelts by Means of a Compound Precursor

Formation of NiFe2O4 Nanoparticles by Mechanochemical Reaction

Synthesis and optical characterization of Co3O4 nanocrystals

Facile Preparation of Co3O4 Nanoparticles Via Thermal Decomposition of Co(NO3)2 Loading on C3N4

Formation of Zinc Oxide Nanoparticles by Mechanochemical Reaction

Synthesis of Cadmium Oxide (cdo) Nanocrystallite and Crystallization Kinetics During Thermal Treatment

Mechanochemical Synthesis of Zinc Oxide Nanocrystalline

Cobalt Ferrite Nanoparticles Prepared by Coprecipitation/Mechanochemical Treatment

Synthesis of Tin Oxide Nanoparticles by Mechanochemical Reaction

Study on Synthesis of Nanocrystalline Co3O4 Powders by Solution Combustion Technique and the Subsequent Heat Treatment Process

Synthesis of ZnFe2O4 Nanocrystallites by Mechanochemical Reaction

Synthesis and Their Physicochemical Behaviors of Flower-Like Co3O4 Microspheres

Mechanochemical Synthesis of Cadmium-Doped Tin Oxide Nanoparticles

Shape-controlled Synthesis of Nanocubic Co3O4 by Hydrothermal Oxidation Method