Abstract:Tricobalt tetraoxide (Co3O4) nanoparticles have excellent applications in the fields of electricity, photocatalysis, and ceramics, whereas conventional synthesis methods require sophisticated equipment, strictly controlled conditions, and long duration. Herein, a new method for the synthesis of Co3O4 nanoparticles was proposed. In this emulsion detonation method, the precursor cobalt nitrate hexahydrate (Co(NO3)2·6H2O) was added during the production of the explosives and was therefore more uniformly dispersed than in other detonation methods. The preparation and detonation durations of the explosives were on the scale of minutes and microseconds, respectively, which are much shorter than those in other nanomaterial synthesis methods. The collected products were briefly purified and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared spectrometer, field emission scanning electron microscopy, and field emission transmission electron microscopy. Cyclic voltammetry and galvanostatic charge–discharge measurements were performed. The results show that the synthesized products were of high purity and consisted mainly of sphere-like particles with a dimensional distribution of approximately 50 nm. The electrochemical properties of these Co3O4 nanoparticles were similar to those synthesized by conventional methods. Combined with the detonation theory and the initial composition of the products, the analysis showed that the synthesis mechanism is mainly divided into two stages: formation and polymerization. Therefore, this approach could provide a new and effective synthesis method for the low-cost production of Co3O4 nanoparticles.

Mechanochemical Route to Synthesize Co 3 O 4 /cuo Composite Nanopowders

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

Synthesis of mesoporous nanocrystalline Co<sub>3</sub>O<sub>4</sub> via an easy and inexpensive method

The Synthesis and Characteristic of Co3O4 Nanocrystals

Synthesis of Co3O4 nanoparticles via an ionic liquid-assisted methodology at room temperature

Characterization and synthesis mechanism of Co3O4 nanoparticles synthesized by the emulsion detonation method

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Synthesis and Their Physicochemical Behaviors of Flower-Like Co3O4 Microspheres

Synthesis and Characterization of Ca3Co4O9 Nanoparticles by Citrate Sol-Gel Method

Novel three-dimensional Co3O4 dendritic superstructures: Hydrothermal synthesis, formation mechanism and magnetic properties

Micelle-assisted hydrothermal synthesis of the uniform Co3O4 nanorods and its chemoluminescence properties of CO oxidation

Decoration of CeO 2 Nanoparticles on Cu/Co Bimetallic Oxide and Their Catalytic Performance

Clean synthesis of Cu 2 O@CeO 2 core@shell nanocubes with highly active interface

Co3O4@CeO2 Core@Shell Cubes: Designed Synthesis and Optimization of Catalytic Properties

Carbonate-Assisted Hydrothermal Synthesis of Nanoporous Cuo Microstructures and Their Application in Catalysis

A facile route to controlled synthesis of Co<sub>3</sub>O<sub>4</sub> nanoparticles and their environmental catalytic properties

Facile mechanochemical synthesis of compositionally complex spinel‐type oxides, (Co, Fe, Mn)3O4, (Co, Fe, Mn, Ni)3O4, (Co, Cr, Fe, Mn, Ni)3O4

Fabrication of Co3o4 Nanorods by Calcination of Precursor Powders Prepared in A Novel Inverse Microemulsion

A green and facile synthesis route of nanosize cupric oxide at room temperature