Abstract:A bulk of single crystals Ca3Ta(Al0.9Ga0.1)(3)Si2O14 (CTAGS) with ordered langasite structure in which 90% of gallium was replaced by aluminum was successfully grown by the Czochralski technique. X-ray power diffraction (XRPD) studies confirm that the CTAGS crystals possess a langasite structure. The lattice parameters are a=8.053 angstrom, c=4.938 angstrom, and V=277.36 angstrom(3). High resolution X-ray diffraction (HRXRD) analysis demonstrates that CTAGS single crystals are free of low angle boundaries. The piezoelectric coefficient d(11), dielectric constant epsilon(11)//epsilon(0), dielectric loss electromechanical coupling factor k(12), mechanical quality factor Q and electric resistivity of X-cut plate of CTAGS were measured from room temperature up to 900 degrees C. d(11), epsilon(11)//epsilon(0) and S-11(E), wore found to increase from 3.99 pC/N to 5.67 pC/N, from 13.7 to 15.4 and from 7.92 pm(2)/N to 8.87 pm(2)/N, respectively. In addition, the as-growth crystal is transparent in the wavelength range of 300-3200 nm and the highest transmittance exceeds 90%. (C) 2014 Elsevier B.V. All rights reserved.

Growth and Dielectric Properties of Ca3NbGa3Si2O14 Crystals

Study on Optical and Thermal Properties of Ca3NbGa3Si2O14 Single Crystals

Growth and characterization of Sr3NbGa3Si2O14 single crystals

Growth, thermal and optical properties of Sr3NbGa3Si2O14 single crystals

The Growth And Properties Of Ca(3)Taga(3)Si(2)O(14) Single Crystals

Bridgman Growth of A Novel Piezoelectric Single-Crystal Material: Ca3nbga3si2o14

Bridgman Growth of a Novel Piezoelectric Single-Crystal Material: Ca<sub>3</sub>NbGa<sub>3</sub>Si<sub>2</sub>O<sub>14</sub>

Growth Of A New Ordered Langasite Structure Compound Ca3taga3si2o14 Single Crystal

Growth and high-temperature electromechanical properties of Ca3NbX3Si2O14 (X=Ga and Al) piezoelectric crystals

Bridgman growth of a novel piezoelectric single-crystal material: Ca 3NbGa3Si2O14

Study on the Growth and Optical Activity of Sr3NbGa3Si2O14 Single Crystals

Bridgman Growth of Sr3NbGa3Si2O14 Single Crystal

Growth and high temperature properties of Ca 3 Ta(Al 0.9 Ga 0.1 ) 3 Si 2 O 14 crystals with ordered langasite structure

Raman Scattering Spectra of Ca3NbGa3Si2O14 (CNGS) Crystals

Study on the Growth and Characterization of Sr3TaGa3Si2O14 Single Crystals

Growth and Piezoelectric Properties of Large Size Ca3Ta(Ga0.5Al0.5)3Si2O14 Crystals with Langasite Structure

Crystal Growth and Characterization of New Piezoelectric Crystals La3Ga5SiO14

Properties of piezoelectric single crystals Ca3TaGa3Si2O14 at high temperature and high vacuum conditions

A Systematic Study on Structure and Optical Properties of A3BGa3Si2O14 Series of Crystals

Preparation and Properties of a Novel Piezoelectric Single-Crystal Material: Sr3TaGa3Si2O14

Growth and Characterization of High Temperature La3Nb0.5Ga5.3Al0.2O14 (LNGA) and La3Ta0.5Ga5.3Al0.2O14 (LTGA) Piezoelectric Single Crystals