Abstract:TiF3-doped NaH/Al mixture was hydrogenated into Na3AlH6 and NaAlH4 complex hydrides by reactive ball-milling at room temperature through the optimization of milling duration and hydrogen pressure. The analysis of the preparation of NaAlH4 samples during reactive ball-milling process has been performed by XRD and TG/DSC. It has been found that Na3AlH6 was formed under 0.5 MPa hydrogen pressure and 30 h milling duration, while NaAlH4 was formed under 0.8 MPa hydrogen pressure and 45 h milling duration. The process of preparing NaAlH4 by ball-milling was found accomplished via two reaction steps, namely: (1) NaH + Al + H-2 Na3AlH6 and (2) Na3AlH6 + Al + H-2 -> NaAlH4. As the hydrogen pressure and milling duration increase, the synthetic yield of NaAlH4 and its corresponding dehydriding capacity are both increased. With increased hydrogen pressure (0.8-3 MPa) and milling duration (45-60 h), the cell volume of Na3AlH6 decreases while that of NaAlH4 increases gradually. The abundance of Na3AlH6 phase decreases from 57.76 (x = 0.8, y = 45) to 8.69 wt.% (x = 3, y = 60), and the abundance of NaAlH4 phase increases from 20.63 (x = 0.8, y = 45) to 86.50 wt.% (x = 3, y = 60). All the samples prepared in this way have fairly good activation behavior and fast hydriding/dehydriding reaction kinetics, which are capable of absorbing 4.26 wt.% hydrogen at 120 degrees C and desorbing 4.12 wt.% hydrogen at 150 degrees C, respectively. The improvement of hydriding/dehydriding properties is ascribed to the favorable microstructure and ultrafine particle features of nanosized NaAlH4 formed during ball-milling at the optimum synthetic condition. (C) 2010 Professor T. Nejat Veziroglu. Published by Elsevier Ltd. All rights reserved.

The Research of Liquid Phase Synthesis of Sodium Aluminum Hydride

Wet Chemical Synthesis of Non-solvated Rod-Like Α'-Alh3 As a Hydrogen Storage Material.

Catalytical Synthesis and In Situ Doping of Sodium Aluminum Hydride from Elements

Conversion of Methyltrichlorosilane in Stirred Bed Reactor by Methylalumminumchloride Method

The Study of the Synthetic of Sodium Aluminum Hydride under Low Pressure

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation of Nano-aluminum Powder in AlCl3-EMIC Ionic Liquid

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Thermodynamic and kinetic study of the thermal dehydrogenation of Sr(AlH 4 ) 2 taking into account the by-products NaCl and LiCl

Hydrogen production from solid reactions between MAlH4 and NH4Cl

Sodium Borohydride Synthesis by Reaction of Na2o Contained Sodium Borate with Al and Hydrogen

Enhanced Thermal Stability and High-Quality of Α-Alh3 Via Crystal Seed Preparation Method

Investigation on the Improved Hydrolysis of Aluminum–calcium Hydride-Salt Mixture Elaborated by Ball Milling

Hydriding-dehydriding Kinetics and the Microstructure of La- and Sm-doped NaAlH4 Prepared Via Direct Synthesis Method

Formation of Na3AlH6 from a NaH/Al Mixture and Ti-containing Catalyst

Synthesis and Hydriding/dehydriding Properties of Nanosized Sodium Alanates Prepared by Reactive Ball-Milling

Synthesis and Hydrogen Desorption Properties of Nanoscale α-AlH 3

Experimental Researches on Hydrogen Generation by Aluminum with Adding Lithium at High Temperature

Influence of Anode Effect on Formation of Hydrogen in Electrolytic Aluminum Liquid

Synthesis and Stability of Hydrogen Storage Material Aluminum Hydride

A comparison study on aluminum-water reaction with different catalysts