HU Zhen

DOI: https://doi.org/10.3969/j.issn.1008-0511.2007.02.008

2007-01-01

Abstract:In this work,nanometer CeO2 particles were prepared by microwave,the materials included cerium sulfate and sodium hydroxide,the surfactant was polyglycol.The effect factors of preparing conditions were investigated respectively.The optimum conditions of synthesis process were obtained by experiments as follows:the molar ratio of reactants was 4.8∶1,the dosage of PEG in the reaction process was 8 mL,the dosage of PEG in the washing process was 7 mL,the dosage of absolute alcohol was 10 mL,the irradiation time was 6 min,the microwave irradiation pressure was 0.14 MPa,the microwave power was 232 W,the ultrasonic wave dispersing time was 10 min and the microwave drying time was 10 min.The product which was produced under optimum condition belonged to the nanometer material,the particles diameter was 24.9 nm.