Corrosion failure analysis of high strength grade super 13Cr-110 tubing string
Shidong Zhu,Jianfeng Wei,Rui Cai,Zhenquan Bai,Genshu Zhou
DOI: https://doi.org/10.1016/j.engfailanal.2011.07.017
IF: 4
2011-01-01
Engineering Failure Analysis
Abstract:The main reasons for corrosion failure of super 13Cr-110 tubing and couplings have been proposed based on the analysis techniques of Optical Microscopy (OM), Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS) and X-ray Diffraction (XRD). The results show that the composition, structure and mechanical properties of the tubing and the coupling were all in accordance with the corresponding parameter requirements of API Spec 5CT standards. Furthermore, corrosion occurring in the inner wall of joint was caused by the combined impacts of CO 2 corrosion, acid corrosion, erosion corrosion, and crevice corrosion, meanwhile, the synergistic effects of crevice corrosion, and sulfate-reducing bacteria (SRB) corrosion resulted in corrosion occurring in the outer wall of the tubing and the coupling. Finally, to check the quality of the tubing string before well completion, increase torque, install a centralizer, and add bactericide and inhibitor were advised to prevent the types of corrosion failure from taking place. © 2011.