Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Effect of Microstructural Features on Fatigue Behavior in A319-T6 Aluminum Alloy

Strain Ratio Effects on Low-Cycle Fatigue Behavior and Deformation Microstructure of 2124-T851 Aluminum Alloy

Microstructural Effects on Short Fatigue Crack Propagation in Cast Al-Si Alloys

Physical essence of long fatigue crack growth behavior for aluminum-lithium alloy

Effect of Fatigue Behavior on Microstructural Features in a Cast Al-12Si-CuNiMg Alloy under High Cycle Fatigue Loading

Crack Initiation and Propagation of Cast A356 Aluminum Alloy under Multi-Axial Cyclic Loadings

Microstructural Influences on the High Cycle Fatigue Life Dispersion and Damage Mechanism in a Metastable Β Titanium Alloy

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Fatigue crack growth behavior of 2624-T39 aluminum alloy with different grain sizes

Comparison of Fatigue Crack Initiation Behavior in Different Microstructures of TC21 Titanium Alloy

Fatigue Behavior and Microscopic Mechanism of 7020 Aluminum Alloy Profile

Proagation Rate of Fatigue Crack of 6156 Aluminum Alloy

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

Microstructure sensitivity of the low cycle fatigue crack initiation mechanisms for the Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study and crystal plasticity simulation

Microstructure Study on Very-High-Cycle Fatigue of an Addi-tively Manufactured Aluminium Alloy Via Advanced Charac-terization Methods

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Effect of Microstructure on Ultra-High Cycle Fatigue Behavior of Ti–6Al–4V

Effect of Aging Conditions on the Fatigue Crack Propagation Rate of 2A97 Aluminum-Lithium Alloy

Effects of Anisotropic Microstructure and Load Ratio on Fatigue Crack Propagation Rate in Additively Manufactured Ti-6Al-4V Alloy

Fatigue Crack Propagation Behavior of 2050 Aluminum Alloy

Micro Porosity and Its Effect on Fatigue Performance of 7050 Aluminum Thick Plates