Versatile Epoxidized Soybean Oil-Based Resin with Excellent Adhesion and Film-Forming Property
Zhang Qian,Shouqing Liu,Guanben Du,Shengtao Wang,Yilin Shen,Xiaojian Zhou,Shuyang Jiang,Hui Niu,Zhigang Duan,Taohong Li
DOI: https://doi.org/10.1021/acssuschemeng.3c00743
IF: 8.4
2023-03-22
ACS Sustainable Chemistry & Engineering
Abstract:Deriving environmentally friendly and renewable polymers from epoxidized plant oils (EPOs) is one of the promising strategies for realizing the sustainable development of materials industry. Direct crosslinking EPOs without pre-modifications is a straightforward, efficient, and cost-effective way for the utilization of EPOs. Herein, a facile and green strategy that crosslinks epoxidized soybean oil with highly branched and flexible polyamine via ring-opening and amidation polymerizations successfully produced a novel resin with exceptional properties and versatile potential applications. After completely cured, the resin appeared to be super strong structural adhesive as it provided a room-temperature bonding strength of 12–24 MPa for metal and non-metal substrates, as well as a steel bonding strength of 11.6 MPa at cryogenic temperature (−196 °C), which is far superior to the previously reported oil-based adhesives. Meanwhile, the resin exhibited excellent film-forming ability. Particularly, by controlling the curing temperature, the films with tunable mechanical properties were obtained with a tensile strength of 3–40 MPa and an elongation at break of 17–230%. The features of uncured resin, including liquid viscoelasticity, good wettability, and high molecular weight, make it a qualified pressure-sensitive adhesive which demonstrated satisfied peel strength for various substrates.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology