Study on contamination–free and transparent two–component PU adhesive

Ying DU,Jianxian GONG,Guosheng GAO
DOI: https://doi.org/10.3321/j.issn:1000-6613.2006.04.019
2006-01-01
Abstract:A two-component,solvent-free,transparent,epoxy resin modified polyurethane adhesive is introduced in this paper.The mechanims of PU/EP synthesis was tracked by IR spectroscopy.The chemical reactions among groups and the change of products with time were analyzed.The result showed that several properties of modified products were greatly improved.Under the suitable raw material ratio and experiment condition,the viscosity,flow ability,stability,storage life,were satisfactory.When PU/EP curing agent was 5∶3,the skin drying time was 45min,the shearing intensity was more than 19MPa,the product was tough,solvent resistant and temperature resistant.During curing process no bubble was created,which was good for usein bonding and sealing.