Abstract:Uniform, large-scale, and well-aligned needle-like ZnO nanorods with good photoluminescence and photocatalysis properties on Zn substrates, have been successfully fabricated using a simple low-temperature seed-layer growth approach in solution (50 °C). The formation of ZnO seed-layer by the anodic oxidation technique (AOT) plays an important role in the subsequent growth of highly oriented ZnO nanorods arrays. Temperature also proved to be a significant factor in the growth of ZnO nanorods and had a great effect on their optical properties. X-ray diffraction (XRD) analysis, selected-area electron diffraction (SAED) pattern and high-resolution TEM (HRTEM) indicated that the needle-like ZnO nanorods were single crystal in nature and that they had grown up preferentially along the [0001] direction. The well-aligned ZnO nanorods arrays on Zn substrates exhibited strong UV emission at around 380 nm at room temperature. To investigate their potential as photocatalysts, degradation of pentachlorophenol (PCP) in aqueous solution was carried out using photocatalytic processes, with comparison to direct photolysis. After 1 h, the degradation efficiencies of PCP by direct photolysis and photocatalytic processes achieved 57% and 76% under given experimental conditions, respectively. This improved degradation efficiency of PCP illustrates that ZnO nanorods arrays on Zn substrates have good photocatalytic activity. This simple low-temperature seed-layer growth approach in solution resulted in the development of an effective and low-cost fabrication process for high-quality ZnO nanorods arrays with good optical and photocatalytic properties that can be applicable in many fields such as photocatalysis, photovoltaic cells, luminescent sensors, and photoconductive sensors.

ZnO Nanorod Arrays and Nanowires by Hydrothermal Growth

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Facile Hydrothermal Synthesis of Large Scale ZnO Nanorod Arrays and Their Growth Mechanism

Growth of Zno Nanorod Arrays on Soft Substrates by Hydrothermal Process

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Synthesis of ZnO Nanorods and Nanorod Arrays Through Hydrothermal Methods

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

A facile route to ZnO nanorod arrays using wet chemical method

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Low temperature growth and properties of ZnO nanorod arrays

Aligned ZnO Nanorods Synthesized by a Simple Hydrothermal Reaction

Hydrothermal Growth and Characterization of ZnO Nanorods

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Fabrication of needle-like ZnO nanorods arrays by a low-temperature seed-layer growth approach in solution

Ordered Growth and Photoluminescence of ZnO Nano-Arrays on Silicon Substrates with Seed Film by Hydrothermal Method

Low-Temperature Synthesis and Optical Property of ZnO Nanorod Arrays

Zno Nanocrystal Arrays Fabricated From Ammonia Solution System

Hydrothermal synthesis of ZnO nanowires and nanobelts on a large scale