Abstract:Nano-scaled pure and iron doping Titanium Dioxide prepared by TiCl4 hydrolysis were obtained. Two methods, step precipitation and co-precipitation, were applied in preparing the iron doping samples. The crystallization and decomposition processes were extensively investigated by methods of X-ray diffraction and TEM. The grain sizes under series of calcinating temperatures were computed according to Voigt function analysis. The results of TEM images also justified the computed grain size. The results showed that Titanium Dioxide prepared by TiCl4 hydrolysis is amorphous, and that no obvious: crystallization temperature or exothermic peaks were observed, contrary to the some previous reports. The computation applying the nuclei growth equation showed that the crystal grain growth of the pure and co-precipitation samples can be divided into 2 steps. The growth activation energy of the former step is 10.7kJ . mol(-1) and 8.6kJ . mol(-1), respectively and that of the latter step is 111.6kJ . mol(-1). As to the step precipitation samples, there showed no obvious difference in crystal growth activation energies for the 2 steps, and for the transformation of anantase to rutile was almost completed before 600 degrees C. There was evidence that the iron doping accelerated the transformation of rutile to anatase and this is especially obvious in step precipitation samples.

Particle Size Control Of Nanocrystalline Anatase Tio2 Synthesized By Hydrolysis Of Titanyl Organic Compounds

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Hydrothermal Synthesis of Titania Powder with Different Particle Sizes

pH control on preparation of nano-TiO_2 by gel-sol process

Synthesis of Size-Controlled Nanotitania Particles via a Simple Sol-Gel Method

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

A study on the synthesis of coarse TiO2 powder with controlled particle sizes and morphology via hydrolysis

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Synthesis of nanometer-sized TiO2 particles by a microemulsion method

Hydrothermal Preparation and Photocatalytic Properties of Quantum Size TiO2 Nanoparticles

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Precisely Controlled Heterogeneous Nucleation Sites for Tio2 Crystal Growth

Controlling the Synthetic Pathways of Tio2-Derived Nanostructured Materials

STUDY ON THE CONTROLLING OF CRYSTALLINE AND THE TRANSFORMATION TEMPERATURE OF NANO-TITANIA POWDER

Synthesis of Crystalline Nanosized Titanium Dioxide Via a Reverse Micelle Method at Room Temperature

A Simple Solution-Phase Route for Room-Temperature Synthesis of Mesoporous and Nanocrystalline Anatase Tio2

Synthesis of Nanosized Rutile TiO2 Powder at Low Temperature

Preparation of Anatase TiO2 Nanocrystalline and Research on Origion of Phase

Synthesis and Characterization of Size-Controlled Titania Nanorods through Double Surfactants