Abstract:Carbon coated LiFePO4 (LiFePO4/C) with different contents of high electron conductive iron phosphide phase was synthesized by an aqueous sol–gel method in a reductive sintering atmosphere. Different synthesis parameters were used for adjusting the microstructure and phase compositions of the products. The effects of the carbon coating and iron phosphides on the electrochemical properties of the LiFePO4/C electrodes were studied by means of testing the discharge capacities at rates of 0.1–5C (1C=170mAhg−1) and analyzing the CV curves. The results show that carbon coating in a content of 1.5wt.% derived from the carbon source of ethylene glycol greatly decreases the particle size of LiFePO4 in one order in the specific surface area, and significantly improves the rate capability of LiFePO4. The effect of the content of FeP on the capacity of the carbon coated LiFePO4 was different at different discharge rates. Increasing the content of FeP from 1.2 to 3.7wt.% slightly decreases the capacity of LiFePO4/C at low discharge rate (0.1C and 1C), but obviously increases the capacity of LiFePO4/C when the discharge rate is increased to 5C. For the carbon free sample, even it also has 1.8wt.% FeP, it still possesses poor capacity due to the large particle size of LiFePO4 and the lack of conductivity. And too much iron phosphides lowers the discharge capacity of the electrode since they are inert for the deinsertion/insertion of lithium ion.

Effects of Solvents and Ph Values on Synthesis of LiFePO4/C Prepared Via a Sol-Gel Route

Synthesis and Characterization of Lifepo4/C Prepared Via A Sol-Gel Method

SYNTHESIS AND CHARACTERIZATION OF <font>LiFePO</font><sub>4</sub>/<font>C</font> PREPARED VIA A SOL–GEL METHOD

Study on the Electrochemical Performance of Carbon-Coated LiFePO4 Prepared by Sol-Gel Method

Effects of Iron Sources on Structure and Electrochemical Properties of LiFePO4/C Prepared by Sol-Gel Method

Effects of Reductive Conditions on the Microstructure and Electrochemical Properties of Sol-Gel Derived LiFePO[sub 4]∕C

Influences of precursor pH value on the sol-gel prepared LiFePO4

Electrochemical Performance of LiFePO 4 /(c+fe 2 P) Composite Cathode Material Synthesized by Sol-Gel Method

Effects of Mechanical Activation of Sol and Different Solvents on the Structure and Electrochemical Properties of LiFePO_4/C Cathode Materials

Enhanced Electrochemical Performance of LiFePO 4 /C Prepared by Sol–gel Synthesis with Dry Ball-Milling

Electrochemical Performance of Nanocrystalline Li3V2(PO4)3/carbon Composite Material Synthesized by a Novel Sol–gel Method

Effect of Synthesis Temperature on the Structure and Electrochemical Performances of LiFePO4/C

Effect of Synthesis Temperature on Electrochemical Performances of LiFePO4/C Composites

Impact of Ph on Morphology and Electrochemical Performance of LiFePO4 As Cathode for Lithium-ion Batteries

Characterization of LiFePO<sub>4</sub> Synthesized by Sol-Gel Processing

Preparation of Lithium Iron Phosphate by Sol-Gel Technique

Inorganic-based Sol–gel Synthesis of Nano-Structured LiFePO 4 /C Composite Materials for Lithium Ion Batteries

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Effects of carbon coating and iron phosphides on the electrochemical properties of LiFePO4/C

Synthesis and Electrochemical Performance of LiFePO4/C Prepared by a New Method

Synthesis of LiFePO 4 /C Composite Electrode with Enhanced Electrochemical Performance