Abstract:series of aluminophosphate-based tubular mesoporous molecular sieves without (UHM-1) and with substituted silicon (UHM-3) have been synthesized at room temperature in the presence of a cationic surfactant cetyltrimethylammonium chloride (CTACl) and an organic base tetramethylammonium hydroxide (TMAOH). Characterization by powder X-ray diffraction (XRD), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), N-2 adsorption, and Al-27, P-31, and Si-29 magic-angle-spinning (MAS) NMR spectroscopies has been carried out to understand both the pore structures and the local atomic arrangements of these solid products. The synthesis of UHM-1 and UHM-3 is successful only at room temperature within the following molar gel composition: Al2O3:(0.6-3.4) P2O5:(0.0-1.0) SiO2:(0.24-0.50) CTACl:(8.5-47.0) TMAOH:(200-642) H2O. The presence of TMAOH is essential to maintain the gel pH at 8.5 or above. The pH greatly influences the nature of the final "crystalline" products, particularly the coordination of aluminum and phosphorus. XRD, EPMA, TEM, and N-2 adsorption measurements show that these solid products have a unique composition and disordered tubular mesopores with an average pore diameter of about 35 Angstrom in the calcined form. The overall P/Al ratio of UHM-1 is less than unity, especially in gels of higher pH, indicating incomplete condensation of phosphorus and a nonideal aluminophosphate framework. This may account for their poorer thermal stability relative to microporous aluminophosphate molecular sieves and aluminosilicate-based MCM-41 materials. Al-27 and P-31 MAS NMR reveal that aluminum in UHM-1 with a P/Al ratio of 0.60 synthesized at a gel pH of 8.5 is present in both tetrahedral and octahedral environments while phosphorus is present in a tetrahedral environment and also as hydroxylated species. As the P/Al ratio of UHM-1 decreases together with increasing gel pH, the relative amounts of tetrahedral aluminum and tetrahedral phosphorus decrease. This change suggests some Al-O-P linkages in the tetrahedral regions of the UHM-1 samples, and an increasing octahedral aluminum content st lower P/Al ratio indicates that octahedral aluminum alone can construct a tubular mesoporous structure. After incorporation of silicon into UHM-1, Si-29, Al-27, and P-31 MAS NMR of UHM-3 reveal that silicon is atomically dispersed and that the relative amounts of tetrahedral aluminum and tetrahedral phosphorus increase monotonically with increasing silicon incorporation. Virtually all the aluminum is tetrahedral, and all the phosphorus is tetrahedral after silicon incorporation reaches a Si/Al ratio of unity. This indicates more ordered atomic arrangements of tetrahedral silicon, aluminum, and phosphorus via oxygen bridges in UHM-3 than in UHM-1. The incorporation of silicon appears to make the aluminophosphate framework more flexible and facilitates the formation of an aluminophosphate-based mesoporous structure.

Synthesis of Mesoporous Aluminophosphate and Silicoaluminophosphate in the Presence of Nonionic Poly(Ethylene Oxide) Surfactant

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Synthesis of the Molecular-Sieve Alpo4-5 with an Unequal Molar Ratio of Al2o3 to P2o5

Generalized Syntheses of Large-Pore Mesoporous Metal Oxides with Semicrystalline Frameworks

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

Bifunctional Hybrid Mesoporous Organoaluminosilicates with Molecularly Ordered Ethylene Groups.

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Synthesis of Mesoporous Silica from Commercial Poly(ethylene Oxide)/poly(butylene Oxide) Copolymers: Toward the Rational Design of Ordered Mesoporous Materials

Characterization of Aluminophosphate-Based Tubular Mesoporous Molecular Sieves

Tubular aluminophosphate mesoporous materials containing framework silicon, vanadium and manganese

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

A vesicle-aggregation-assembly approach to highly ordered mesoporous γ-alumina microspheres with shifted double-diamond networks.

Synthesis of Aluminophosphate Molecular Sieves in Alkaline Media

A Facile Rout to Synthesis Lamellate Structure Mesoporous Alumina Using Polyethylene Glycol 6000 (PEG, Molecular Weight = 6000) As Structure Directing Agent