Abstract:The skeletal Ni P amorphous alloy(Raney Ni P) was prepared by alkali leaching a Ni P Al amorphous alloy obtained by the rapid quenching technique. Its amorphous structure was confirmed by both the XRD and EXAFS. By using liquid phase benzene hydrogenation, an important reaction in industrial production, the selectivity to cyclohexane and the catalytic activity(including hydrogen uptake rate, reaction conversion and TOF value) of the as prepared Raney Ni P catalyst were measured. In comparison with the corresponding Ni P amorphous alloy obtained via the traditional rapid quenching technique, the crystallized Raney Ni P, and Raney Ni which was widely used in industry, the Raney Ni P catalyst exhibited much higher activity besides the perfect selectivity to cyclohexane. The DSC analysis also revealed its high thermal stability. These results demonstrated its potential application in industrial processes. By measuring the effects of the benzene concentration, the hydrogen pressure, and the reaction temperature on the hydrogenation rate, the reaction kinetics and the apparent activation energies were determined, based on which, a plausible mechanism was proposed. The higher activity of Raney Ni P than that of traditional Ni P was mainly due to its higher surface area. While the higher activity of Raney Ni P than that of Raney Ni was mainly attributed to the nature of the active sites. Since no significant electronic interaction between Ni and P in Ni P amorphous alloy was found by XPS spectra, the geometric effect was considered as the main promoting effect, which was briefly discussed according to various characterizations, such as ICP, XRD, EXAFS, BET, and hydrogen chemisorption. The crystallization deactivation of Raney Ni P amorphous alloy was attributed to the change in both the surface area and the structure of the active sites.

Skeletal Ni-P Amorphous Alloy (R-Ni-p) As A Hydrogenation Catalyst

Selective Hydrogenation of Adiponitrile over a Skeletal Ni–P Amorphous Catalyst (raney Ni–P) at 1atm Pressure

Preparation of skeletal Ni-P amorphous alloy and the study of its catalytic properties during benzene hydrogenation

Skeletal Ni Catalyst Prepared from a Rapidly Quenched Ni–Al Alloy and Its High Selectivity in 2-Ethylanthraquinone Hydrogenation

Structural and Catalytic Properties of Skeletal Ni Catalyst Prepared from the Rapidly Quenched Ni50al50 Alloy

Skeletal Ni Catalysts Prepared from Ni–Al Alloys Rapidly Quenched at Different Rates: Texture, Structure and Catalytic Performance in Chemoselective Hydrogenation of 2-Ethylanthraquinone

Research, Development, and Application of Amorphous Nickel Alloy Catalysts Prepared by Melt-Quenching

Glucose Hydrogenation to Sorbitol over a Skeletal Ni-P Amorphous Alloy Catalyst (raney Ni-P)

Selective Hydrogenation of Adiponitrile over a Raney Ni–P Amorphous Catalyst

Preparation of novel Raney-Ni catalysts and characterization by XRD, SEM and XPS

Modification on Ni-P Amorphous Catalyst with Sio2 and Pd

Ordered Mesoporous Ni Nanowires with Enhanced Hydrogenation Activity Prepared by Electroless Plating on Functionalized SBA-15

Thermal Stability of Skeletal Rapidly Quenched Ni Catalyst

Amorphous Alloy Deposited on Support and Its Hydrogenation Activity

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Skeletal Nickel Catalysts Prepared from Rapidly Quenched Ni‐Alloys

Xps Studies On Surface Electronic Characteristics Of Ni-B And Ni-P Amorphous Alloy And Its Correlation To Their Catalytic Properties

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Study On The Crystallization Process Of Ni-P Amorphous Alloy

Amorphous NiP Supported on Rgo for Superior Hydrogen Generation from Hydrolysis of Ammonia Borane

Top-Down Syntheses of Nickel-Based Structured Catalysts for Hydrogen Production from Ammonia