Intrinsic exciton photophysics of PbS quantum dots revealed by low-temperature single nanocrystal spectroscopy.
S. Krishnamurthy,Zhongjian Hu,Ajay Singh,A. Malko,J. Hollingsworth,M. Nestoklon,H. Htoon,I. Avdeev,S. Goupalov,Younghee Kim
DOI: https://doi.org/10.1021/acs.nanolett.9b02937
2019-11-12
Abstract:With a tunable size-dependent photoluminescence (PL) over a wide infrared wavelength range, lead chalcogenide quantum dots (QDs) have attracted significant scientific and technological interest. Nevertheless, the investigation of intrinsic exciton photophysics at the single-QD level has remained a challenge. Herein, we present a comprehensive study of PL properties for individual core/shell PbS/CdS QDs emissive near 1.0 eV. In contrast to the sub-meV spectral linewidths observed for II/VI QDs, PbS/CdS QDs are predicted to possess broad homogeneous linewidths. Performing spectroscopy at cryogenic (4 K) temperatures, we provide direct evidence confirming theoretical predictions, showing that intrinsic linewidths for PbS/CdS QDs are in the range of 8-25 meV, with an average of 16.4 meV. In addition, low-temperature, single-QD spectroscopy reveals a broad low-energy side emission attributable to optical as well as localized acoustic phonon-assisted transitions. By tracking single QDs from 4 K to 250 K we were able to probe tempera-ture-dependent evolutions of emission energy, linewidth and line shape. Finally, polariza-tion-resolved PL imaging showed that PbS/CdS QDs are characterized by a 3D emission dipole, in contrast with the 2D dipole observed for CdSe QDs.
Physics,Medicine,Materials Science