Abstract:CdSe1-xSx nanocrystals were grown by annealing silica glass wit h supersaturate Cd,Se and S at 500～800℃ for 4h, respectively. The absorption and p hotolumines cence (PL) of the nanocrystals excited with light of different wavelength were m easu red at room temperature. The PL spectra were discussed. In the sample annealed a t 550℃, no absorption and emission were observed in the range of 300～ 800nm. This suggested that no CdSe1-xSx nanocrystals formed. The a bsorption of 1S3/21Se shifted toward to red with the rising of growth temperatures from 600～800℃ due to the weakening of quantum confinement with the increase of nanocrystal sizes. Ma inly broadened peaks named H and L bands, H band corresponding to rec ombination at the band edge and L band corresponds to radiative recombination as sociated with deep traps, were observed in the grown at 600～650℃ . As the growth temperature was raised higher, L bands disappeared gr adually and only H bands were observed. This indicated that deep trap density de creased with the increase of growth temperature and the deep traps mainly were s urface states. H bands shifted red with the increase of nanocrystal growth tempe ratures. This was due to quantum size effects because nanocrystal mean size incr eased with the increase of growth temperature. In the nanocrystals grown at 650 ～ 800℃, a series of obvious small peaks superposed on the broadened bands were al so observed. The peak energy for nanocrystals grown at different temperatures wa s similar and only new peaks were observed in samples grown at lower temperature s. The superposed peaks could be divided into two groups. Within each group, the peaks distributed periodically with energy separation of 120meV. There was 50me V energy separation between the two groups. The energy separation was much hig her than that of LO phonon. Sizeselective PL spectra of nanocrystals collected using excitation wavelength between 488～650nm indicated that the superposed pea k energy did not change with the excited wavelength, only the relative intensity varied with the excitation wavelength. 

Photoluminescence from colloidal CdS-CdSe-CdS quantum wells

Photoluminescence from Colloidal CdS-CdSe-CdS Quantum Wells

Exciton Radiative Recombination in Spherical CdS∕CdSe∕CdS Quantum-Well Nanostructures

Temperature dependent photoluminescence of single CdS nanowires

Temperature-Dependent Photoluminescence of ZnCuInS/ZnSe/ZnS Quantum Dots

Mid-Infrared Photoluminescence of Pbse/Pbsrse Multiple Quantum Wells Grown by Molecular Beam Epitaxy

Photoluminescence of CdSeS Nanocrystals at Room Temperature

Effects of Core Size and Shell Thickness on Luminescence Dynamics of Wurtzite Cdse/Cds Core/Shell Nanocrystals

Optical Characterization of Bare CdSe and CdSe/CdS Core/shell Nanocrystals

Temperature-dependent photoluminescence of CuInS2 quantum dots

Exciton-related photoluminescence and lasing in CdS nanobelts

Sharp Photoluminescence of CdSeS Nanocrystals Embedded in Silica Glass

Temperature Dependence Of Photoluminescence Properties Of Cds(X)Se(1-X) Quantum Dots Prepared On Silicon Substrate

Studies of Photoluminescence and Microcavity Properties of One-Dimensional CdS Nanostructures

Temperature-Dependent Photoluminescence of CdS/ZnS Core/Shell Quantum Dots for Temperature Sensors

Temperature Dependence of Photoluminescence from Self-Organized Ge Quantum Dots with Large Size and Low Density

Temperature and Composition Dependence of Photoluminescence Dynamics in CdSxSe1−x (0 ≤ X ≤ 1) Nanobelts

Photoluminescence Characteristics of ZnCuInS-ZnS Core-Shell Semiconductor Nanocrystals

Study of Photoluminescence of CdS/ZnS Core/Shell Quantum Dots

Temperature Dependence of Photoluminescence in CdS Nanocrystals Prepared by the Sol-Gel Method

Revealing Mechanisms Of Pl Properties At High And Low Temperature Regimes In Cdse/Zns Core/Shell Quantum Dots