Research on the oxidation characteristics of aluminum flakes of DSC/DTG method

WANG Mou,LIANG Hui-min,XU Jing

DOI: https://doi.org/10.3969/j.issn.1009-6094.2013.02.044

2013-01-01

Abstract:The paper is aimed at introducing our analysis findings on the oxidation characteristics of the aluminum powder in the atmospheric environment through comparison and analysis at different heating rates.As is known,it is necessary to study the energy output law of the metal cloud burst fuels because it contributes to the formulation design of high-energy activities of metal cloud bursts.Such laws can be found by using differential scanning calorimetry method and thermal gravimetric analysis in accordance with the chemical reaction kinetic parameters and chemical reaction thermodynamic parameters of the highly active metal cloud bursts pharmacy of different particle sizes,different proportions and different atmospheric environments.By using the DSC and DTG methods,we can also analyze the thermal response characteristics of aluminum powder in atmospheric environment.As the result of our analysis,we have discovered that the size of the aluminum flake is about 100 nanometers and the aluminum flake can be heated at a rate of 10 ℃/min,9 ℃/min,8 ℃/min and 7 ℃/min.When the experimental data were treated with Kissinger equation and Ozawa equation,the apparent activation energy worked out prove to be similar.The results of our experimental tests indicate that there exist two oxidation processes in the natural environment.When the temperature changes from 650 ℃ to 700 ℃,there might appear a small endothermic peak,because the aluminum surface may get oxidized and form a dense oxide layer to prevent the internal aluminum from further oxidation.The peak seems to be caused by the melting of the internal aluminum content.And,then,with the rise of the surrounding temperature,the oxide layer of film tends to split and the internal structure of the aluminum would begin to get oxidized,thud resulting in the second exothermic peak.Compared with the secondary oxidation peak appearance,the exothermic peak corresponding to the first oxidation process turns to be sharper and stronger,expanding its area significantly.Thus,we know that the first oxidation process tends to release higher amount of heat and can be taken as the main stage of exothermic oxidation.In our experiments,we have discovered apparent activating energy of aluminum oxidation reaction,which has been worked out at about 131.2 kJ/mol,with the apparent pre-exponential factor A being 2.377×1010 s-1 and the order of chemical reactions being 3/2.