Abstract:Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.

Room-temperature fabrication of highly oriented ZnO nanoneedle arrays by anodization of zinc foil

Controlled one-step fabrication of highly oriented ZnO nanoneedle/nanorods arrays at near room temperature.

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

A template-free electrochemical deposition route to ZnO nanoneedle arrays and their optical and field emission properties

Fabrication of oriented ZnO nanorod arrays and their optical performances

Large-Scale and Rapid Synthesis of Ultralong ZnO Nanowire Films via Anodization

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

4 Nm ZnO Nanocrystals Fabrication Through Electron Beam Irradiation on the Surface of a ZnO Nanoneedle Formed by Thermal Annealing

Room-temperature ferromagnetic Co-doped ZnO nanoneedle array prepared by pulsed laser deposition

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Fabrication of ZnO Nanowires by Vapor-Phase Deposition and Their Field Emission Properties

Oriented Nanofibers by a Newly Modified Electrospinning Method

Electrochemical/Chemical Synthesis of Highly-Oriented Single-Crystal Zno Nanotube Arrays on Transparent Conductive Substrates

Synthesis of Monodispersed Zno Nanorod Array Films by Chemical Solution Deposition.

Fabrication and optical property of ZnO nanorod array by hydrothermal method

Fabrication and Field Emission Properties of ZnO Nanorod Arrays with Different Orientation Degrees

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Field Emission Properties of Well-Ordered Zno Nanoneedle Arrays