Deposition and Properties of DLC Film on the Inner Wall of a 10-m-Long Stainless-steel Tube
Pengli Jin,Xiubo Tian,Chunzhi Gong
DOI: https://doi.org/10.11933/j.issn.1007-9289.20230227003
2023-01-01
China surface engineering
Abstract:During industrial production, the inner wall of a tube is often corroded and worn by the conveying material; therefore, it must be protected. Currently, research on the coating of the inner wall of a tube is limited, and research regarding the performance of the inner wall of a large-aspect-ratio tube is lacking. Thus, this study attempts to solve the problem of a diamond-like carbon(DLC) film on the inner wall of a long tube. Herein, the internal surface of a 304 stainless-steel tube, which is 10 m long and 100 mm in diameter, is coated with DLC using plasma-enhanced chemical vapor deposition(PECVD). The hollow cathode discharge of gas into the tube, brightness of the film, contact angle, surface hardness, friction factor, and Raman spectroscopy results are characterized using different tests. During the preparation of the inner coating, the plasma spectrum in the 300-800 band at position 3 of the pipe is analyzed using a spectrometer and optical focusing platform. After the film is prepared, its surface brightness is measured using a color difference meter to determine the L*, a*, and b* values of the film, where L* represents the brightness, a* represents red and green, and b* represents yellow and blue. Scanning electron microscopy(SEM) is used to observe the section morphology of the film. The surface roughness of the film is measured using atomic force microscopy(AFM). A friction and wear-testing machine is used to test the wear resistance of the film. A GCr 15 ball with a diameter of 3 mm is selected as the grinding pair, and the experimental parameters of load, rotational speed, and test time are set as 3 N, 200 r / min, and 120 min, respectively. A nanoindentation hardness instrument is used to measure the nanohardness of the film. A measuring meter for the static contact angle of water is used for measurement; the measurement requires 2 mu l of each drop. Each sample is tested three times, and the average value is calculated as the final test result. The film is measured by a laser Raman spectrometer using a 532 nm laser source from 800 to 2 000 cm(-1), and a Gaussian curve is employed to fit the Raman spectrum. The results demonstrate that in the coating process of the inner wall, the first step is the entry of Ar gas into the pipe for glow discharge cleaning. Ionization and excitation occur during the process of Ar gas discharge, thereby producing Ar+ and Ar-0; additionally, C-2, H, and CH decompose from acetylene. The SEM results of the cross-sections of the films at different positions reveal that the cross-section of the film is uniform and dense, with no cracks, pinholes, or other defects. Further, no cracks are observed in the binding transition between the film and matrix, thickness of the film at different positions, and thickness of the film near the ends of the pipeline, thus indicating that the plasma density in this region and the deposition rate of the film are high. The largest L* and Delta E* values of the film are 37.4 and 1.9, respectively. The AFM results demonstrate larger bulges on the film surface at positions 3 and 7, which result in high surface-roughness, and uniform distribution of the bulges at positions 3 and 9. The water contact angles of the films are smaller at both ends. The results of the wear tests indicate that the friction factor of the film decreases in the first 20 min from 0.225 to approximately 0.175. For a prolonged time, the friction factor remains stable at 0.17. The hardness of the film near the ends of the pipe is slightly higher. Further, no damage or film-peeling is noted in the pin-on-disk test, and the film is characterized as having a good wear resistance. The Raman spectra of the films at different positions reveal that in contrast to positions 1 and 9, the G peaks at positions 3 and 7 exhibit a shift toward the peak level, thus indicating a high stress in the film at both ends. Considering the distribution trend of I-D / I-G in the film, a low ratio of I-D / I-G is determined at both ends of the tube. The glow discharge and DLC deposition in the long tube with a large length ratio provides theoretical support and technical guidance for the uniform coating of the walls of long pipes.