Abstract:Indentation creep testing and uniaxial creep testing were carried out in this paper in order to set up the relationship between them. The aim of this work is to present a experimental validated method to determine the material creep parameters (nm, creep stress exponent; cm, creep factor, ε˙=cmσnm, ε˙, tensile creep strain rate at the steady state; σ, creep stress, usually from the uniaxial tensile testing) from the indentation creep testing. Aluminum alloy 2A12 was tested in this paper. Firstly, a set of indentation creep testing was carried out at 200°C with a flat cylindrical indenter. The net indentation creep stresses were between 905.4 and 1414.8MPa. The steady indentation creep rates in different indentation stresses were obtained, from which the indention creep parameters (d˙=cIσNnI, d˙, the indentation creep depth rate at the steady state; σN, the net section stress; nI, indentation stress exponent; cI, indentation factor) can be derived. The indentation creep testing was simulated by the finite element method. In order to validate the method, a set of uniaxial tensile creep testing was carried out at the same temperature, i.e. 200°C. From the uniaxial tensile creep results, the material creep parameters (ε˙=cmσnm) were also derived. It is shown that the stress exponent determined from indentation and uniaxial creep testing is same, respectively, at a same temperature. A method has been presented to set up the relationship between the indentation creep parameters (d˙=cIσNnI) and uniaxial creep parameters (ε˙=cmσnm) based on a conversion factor. With the indentation creep testing results in conjunction with finite element creep analysis, the material creep parameters (nmI-FEM and cmI-FEM) have also been derived. It can be concluded that the indentation creep testing can been used to determine the creep parameters (nm and cm). The most important conclusion is that the indentation creep exponent is equal to the material creep exponent, nm=nI.

Indentation Creep-Fatigue Test on Aluminum Alloy 2A12

Prediction of Creep Residual Life of Aluminum Alloy 2A12 by Using Indentation Test Method with Flat Cylindrical Indenters

EXPERIMENTAL AND NUMERICAL STUDY ON INDENTATION CREEP WITH A FLAT INDENTER

A Numerical Study of Indentation Creep Using Indenters of Different Geometry

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Indentation Behavior of Aluminum Alloy with Inclusions

Determination of creep parameters by the indentation creep testing in combination with finite element method

Experimental and numerical study of the method to determine the creep parameters from the indentation creep testing

Use of Instrumented Micro-Indentation to Study the Mesoscopic Elasto-Plastic Behavior of Gh4145/Sq Superalloy During High-Temperature Cyclic Straining

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Finite Element Analysis of the Creep Damage Indentation Testing with Flat Indenter

Numerical Investigation of Indentation Fatigue on Polycrystalline Copper

Study of Crystallographic Creep Parameters of Nickel-Based Single Crystal Superalloys by Indentation Method

Characterization of Cyclic Dynamic and Creep Responses of Pure Aluminum by Instrumented Indentation

Creep Aging Research and Macro and Micro Constitutive Modelling of 2219 Aluminum Alloy

An Indentation Fatigue Depth Propagation Law

A New Method to Determine Material Creep Parameters Based Flat Cylindrical Indentation Test

Study of the Ratcheting by the Indentation Fatigue Method with a Flat Cylindrical Indenter: Part I. Experimental Study

Indenter Load Effects on Creep Deformation Behavior for Ti-10V-2Fe-3Al Alloy at Room Temperature

Study on the Indentation Creep Behavior of Mg-4Al-RE-0.8Ca Magnesium Alloy

Fatigue Fracture Analysis on 2524 Aluminum Alloy with the Influence of Creep-Aging Forming Processes