Effect of Initial States on Creep Aging Behaviors and Mechanical Properties of 2124 Aluminum Alloy

ZHAO Jian-hua,CHEN Ze-yu,LI Si-yu,YANG Jin-long,DENG Yun-lai

DOI: https://doi.org/10.3969/j.issn.1001-4381.2012.10.014

2012-01-01

Abstract:Creep aging behaviors and mechanical properties of 2124 aluminum alloy sheets have been studied by optical microscopy(OM),transmission election microscopy(TEM),creep and tensile test,et al.The results show that when the creep aging at 185℃/150MPa,the turning point between the first stage and the second one along the creep curve is easily observed for the samples with an initial state of solution-water quenching(QCA),the characters of TEM micrographics show that the dislocation multiplication(DM) and the balance between DM and dislocation annihilation(DA) occur.While the turning point along the creep curve is difficultly identified for the samples with the initial state of solution-water quenching-rolling to thickness reduction rate of 8%(PCA),the microstructures of TEM reveal that DA mainly occurs.During the processes of creep-aging,it is found that the precipitating S′ phase particles always nucleate with dislocation lines,and their orientations are effected by characteristics of dislocation moving.During PCA process,the existing of dislocation tangling by the rolling before the creep aging supports precipitating S′ phase on vertical {210} planes,therefore,the stress orientated effect of S′ phase is restrained.The mechanical properties of PCA sample are well than that of the as T6 and T87,and the anisotropy of mechanical properties is less than that of the as QCA.