Abstract:Ceramics of the series (0.97- x )Bi 1/2 Na 1/2 TiO 3 - x Bi 1/2 K 1/2 TiO 3 -0.03NaNbO 3 ( x = 0, 0.02, 0.06, 0.10, 0.16, 0.20, 0.30) were prepared by the conventional mixed oxide method. Influence of Bi 1/2 K 1/2 TiO 3 content on the crystal structure, microstructure, dielectric and piezoelectric properties were studied. All compositions showed single perovskite phase and the morphotropic phase boundary (MPB) between rhombohedral and tetragonal phase existed at the point of x = 0.16. Temperature dependences of permittivity and dissipation factor of unpoled samples revealed that permittivity increased with Bi 1/2 K 1/2 TiO 3 content and it reached maximum value near the MPB. At the same time, the peak value of dissipation factor increased with the addition of Bi 1/2 K 1/2 TiO 3 . All the samples experienced two phase transitions: from ferroelectric to antiferroelectric at the first transition temperature ( T d ) and from antiferroelectric to paraelectric at the temperature ( T m ) corresponding to maximum value of permittivity. The phase transition from ferroelectric to antiferroelectric had relaxor characteristic and T d shifted to lower temperature while increasing Bi 1/2 K 1/2 TiO 3 content. The best piezoelectric properties were obtained in 0.81Bi 1/2 Na 1/2 TiO 3 -0.16Bi 1/2 K 1/2 TiO 3 -0.03NaNbO 3 ceramic with a piezoelectric constant ( d 33 ) of 146pC/N, planar electromechanical coupling factor ( k p ) of 30.3% and thickness electromechanical coupling factor ( k t ) of 53.2%. Abnormal piezoelectric properties were observed in the sample ( x = 0.20), which was attributed to the co-existence of ferroelectric and antiferroelectric phases in it.

Dielectric Properties of Bi 4− X La X Ti 3 O 12 (0 ≤ X ≤ 2) Ceramics

Dielectric properties of La3+ substituted BaBi8Ti7O27 ceramics

Processing and Properties of Ferroelectric Bi4-x La Xti3o12 Ceramics

Phase Transition, Dielectric Relaxation and Piezoelectric Properties of Bismuth Doped La2ti2o7 Ceramics

Structural Evolution, Electrical Properties and Electric-Field-induced Changes of (0.8− X )pbtio 3 – X BiFeO 3 –0.2bazro 3 System Near the Morphotropic Phase Boundary

Temperature-stable Dielectric Ceramics in Ba4Nd2Ti4Ta6O30/(La0.1Bi0.9)2Ti2O7 Biphase System

Ferroelectric and Dielectric Properties of La/Mn Co-Doped Bi4ti3o12 Ceramics

Dielectric properties of bismuth doped Ba1-xCaxTiO3 ceramics

Processing and Properties of Ferroelectric Bi4-Xlaxti3o12 Ceramics

Dielectric and energy storage properties of the (1-x)BaTiO3-xBi(Li1/3Hf2/3)O3 (0.08 ≤ × ≤ 0.14) ceramics

Dielectric and Magnetic Properties of (Bi1-xLaxFeO3)0.5(PbTiO3)0.5 Ceramics Prepared from Mechanically Synthesized Powders

Dielectric Behavior of La 2 O 3 -Modified 0.4(ba 0.8 Ca 0.2 )tio 3 –0.6bi(mg 0.5 Ti 0.5 )O 3 Lead-Free Ceramics

Multiferroic and dielectric properties of Bi4LaTi3FeO15 ceramics

Structures and Dielectric Properties of La-Substituted SrBi8Ti7O27 Ceramics

Ferromagnetic, Ferroelectric Properties, and Magneto-Dielectric Effect of Bi4.25La0.75Fe0.5Co0.5Ti3O15 Ceramics

Dielectric and piezoelectric properties of (0.97- x ) Bi 1/2 Na 1/2 TiO 3 - x Bi 1/2 K 1/2 TiO 3 -0.03NaNbO 3 ceramics

Dielectric and Ferroelectric Properties of La-Doped SrBi2Nb2O9 Ceramics

Dielectric and Ferroelectric Properties of (Bixba1−x)(znx/2ti1−x/2)o3ceramics

High Dielectric Strength and Energy Storage Density in Ba6−3xLn8+2xTi18O54 (ln = La, Sm) Low-Loss Dielectric Ceramics

Domain Structure-Dielectric Property Relationship in Lead-Free (1−x)(bi1/2na1/2)tio3xbatio3 Ceramics

Dielectric, Ferroelectric, and Photovoltaic Properties of La-doped Bi(Ni2/3Ta1/3)O3–PbTiO3 Ceramics