Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Influence of Cathode Protection on Corrosion Resistance of Q235 Steel in Lanzhou Soil

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

EFFECTS OF CATHODIC PROTECTION ON CORROSION OF Q235 STEEL IN SRB CONTAINING SOILS

Corrosion Behavior of 35crmn and Q235 Steel in Simulated Acid Rain Conditions

Corrosion Behavior of Q235 in Simulated Natural Environment by Electrochemical Technology

Corrosion of Q345B Steel in Soil Solution Extract Containing Chloride Ions

Corrosion Behavior of Q235 Steel in Atmospheres Containing SO2 and NaCl

Study On Atmospheric Corrosion Behavior Of Q235 Galvanized Steel In Substation

Corrosion Behaviors of Several Kinds of Arc Sprayed Metal Coatings in Simulated Acid Soil Solution

A comparative study on the corrosion behavior of Q235 steel in saturated acidic red and yellow soils

Corrosion behaviors of arc spraying single and double layer coatings in simulated Dagang soil solution

Stray Current Corrosion of Q235 Steel in Hainan Soil

Electrochemical Corrosion Behavior of Arc Sprayed Zn and Zn15Al Coatings in Simulated Salina Soil and Neutral Meadow Soil Solutions

Corrosion Behavior of Q235B Steel and L245 Steel in Dalian Soil Saturated with Water

Experimental study on Q235 steel in soil polluted by NaCl after corrosion

Comparative Study on the Corrosion Behaviours of High-Silicon Chromium Iron and Q235 Steel in a Soil Solution

Investigation of Q235 steel electrochemical corrosion behavior in naturally dried sandy soil

Cathodic Protection of X65 Carbon Steel in a Simulated Oilfield Produced Water

Corrosion Behavior on Carbon Steel in a Simulated Soil Solution under the Interaction Effect of Chloride and Bicarbonate Ions

Cathodic Reactions Involved in the Corrosion of X80 Steel in Acidic Soil Simulated Solution

Corrosion Behaviour of Arc Sprayed Zn55Al Coatings on Q235 Steel in 3.5 wt% NaCl Solution